Abstract:A one-step sintering process was developed to produce magnetocaloric La(Fe,Si)13/Ce-Co composites. The effects of Ce2Co7 content and sintering time on the relevant phase transformations were determined. Following sintering at 1373 K/30 MPa for 1–6 h, the NaZn13-type (La,Ce)(Fe,Co,Si)13 phase formed, the mass fraction of α-Fe phase reduced and the CeFe7-type (La,Ce)(Fe,Co,Si)7 phase appeared. The mass fraction of the (La,Ce)(Fe,Co,Si)7 phase increased, and the α-Fe phase content decreased with increasing Ce2Co7 content. However, the mass fraction of the (La,Ce)(Fe,Co,Si)7 phase reduced with increasing sintering time. The EDS results showed a difference in concentration between Co and Ce at the interphase boundary between the 1:13 phase and the 1:7 phase, indicating that the diffusion mode of Ce is reaction diffusion, while that of Co is the usual vacancy mechanism. Interestingly, almost 100 % single phase (La,Ce)(Fe,Co,Si)13 was obtained by appropriate Ce2Co7 addition. After 6 h sintering at 1373 K, the Ce and Co content in the (La,Ce)(Fe,Co,Si)13 phase increased for larger Ce2Co7 content. Therefore, the Curie temperature increased from 212 K (binder-free sample) to 331 K (15 wt.% Ce2Co7 sample). The maximum magnetic entropy change (−ΔSM)max decreased from 8.8 (binder-free sample) to 6.0 J/kg·K (15 wt.% Ce2Co7 sample) under 5 T field. High values of compressive strength (σbc)max of up to 450 MPa and high thermal conductivity (λ) of up to 7.5 W/m·K were obtained. A feasible route to produce high quality La(Fe,Si)13 based magnetocaloric composites with large MCE, good mechanical properties, attractive thermal conductivity and tunable TC by a one-step sintering process has been demonstrated.

Improvement in the Magnetocaloric Properties of Sintered La(Fe,Si)13 Based Composites Processed by La-Co Grain Boundary Diffusion

Improvement in Mechanical and Magnetocaloric Properties of Hot-Pressed La(Fe,Si)13/La70Co30 Composites by Grain Boundary Engineering

Synthesis and properties of La-Fe-Si/La-Co magnetocaloric composites

Microstructure, Phase Evolution and Magnetocaloric Properties of LaFe11.6Si1.4/La70Co30 Composite

One-Step Sintering Process for the Production of Magnetocaloric La(Fe,Si)13-Based Composites

Superior Properties of LaFe11.8Si1.2/La65Co35 Magnetocaloric Composites Processed by Spark Plasma Sintering

Table-like magnetocaloric effect and enhanced refrigerant capacity of HPS La(Fe,Si)13-based composites by Ce–Co grain boundary diffusion

Mechanisms of rapid magnetocaloric enhancement of La–Fe–Co–Si alloy by high-temperature hot compression with large deformation

Superior comprehensive properties of LaFe11.8Si1.2/Ce60Co40 magnetocaloric composites

Superior Comprehensive Properties of LaFe 11.8 Si 1.2 /ce 60 Co 40 Magnetocaloric Composites

High Density La-Fe-Si Based Magnetocaloric Composites with Excellent Properties Produced by Spark Plasma Sintering

Near room temperature LaFe11.6Si1.4/PrxCo7 magnetocaloric composites with excellent mechanical and thermal properties

Microstructure, Magnetocaloric and Mechanical Properties of LaFe 11.8 Si 1.2 /Y 64 Co 36 Composites Prepared by Hot Pressing and Diffusion Annealing

LaFe11.6Si1.4/Pr40Co60 Magnetocaloric Composites for Refrigeration Near Room Temperature

Microstructural Evolution, Magnetocaloric Effect, Mechanical and Thermal Properties of Hot-Pressed LaFe11.6Si1.4/Ce2Co7 Composites Prepared Using Strip-Cast Master Alloy Flakes

Attractive Properties of Magnetocaloric Spark Plasma Sintered LaFe11.6Si1.4/Pr2Co7 Composites for Near Room Temperature Cooling Applications

Near Room Temperature LaFe 11.6 Si 1.4 /pr X Co 7 Magnetocaloric Composites with Excellent Mechanical and Thermal Properties

A High-Throughput Study of Magnetocaloric Materials: Gradient Solidification Applied to La-Fe-Si

On the microstructural evolution and accelerated magnetocaloric phase formation in La-Fe-Si alloys by hot forging deformation

Rapid Formation of the Magnetocaloric Phase in La-Fe-Co-Si Magnetocaloric Alloys for Near Room Temperature Applications

A Reliable Route for Relieving the Constraints of Multi-Main-phase Nd–La–Ce–Fe–B Sintered Magnets at High La–Ce Substitution: (pr, Nd)H Grain Boundary Diffusion