Organic-Inorganic Hybrid (Beta-Fe3se4)(4)[Fe(Teta)(1.5)] (Teta = Triethylenetetramine) Nanoplates: Solution Synthesis And Magnetic Properties

Desheng Pan,Yong Li,Zheng Han,Bing Li,Chinwei Wang,Teng Yang,Da Li,Chuljin Choi,Zhidong Zhang

DOI: https://doi.org/10.1021/acs.chemmater.8b04814

IF: 10.508

2018-01-01

Chemistry of Materials

Abstract:Incorporation of distinct organic molecules and inorganic fragments into a single crystalline lattice of organic-inorganic hybrid magnets has aroused much attention for novel physical properties and applications. Yet, there has been no report on the discovery of ordered organic-inorganic hybrid magnets with room-temperature magnetism. Here, we report a simple chemical solution method for synthesis of new organic-inorganic hybrid magnets built by organic Fe(teta)(1.5) and inorganic FeSex segments. By changing the reaction temperature, the size of these hybrid nanostructures can be tuned from 100 nm to 4 mu m, and their shapes vary from nanoparticles and nanobelts to nanoplates. Selected area electron diffraction and X-ray diffraction reveal that hybrid (beta-Fe3Se4)(4)[Fe(teta)(1.5)] nanoplates are a single phase in a tetragonal crystal structure with the space group I4cm (108). The thermal magnetic curve between 5 and 900 K was characterized using a vibrating sample magnetometer, revealing room-temperature ferrimagnetism of the (beta-Fe3Se4)(4)[Fe(teta)(1.5)] nanoplates with the Curie temperature (T-C) higher than 530 K. In the case of hybrid nanoplates synthesized at 483 K, a giant coercivity value reaching 11 kOe is obtained at 5 K. Our study not only provides guidance for developing a chemical solution method for controllable fabrication of a new class of organic-inorganic hybrid materials but also enhances the magnetic ordering temperature of such magnetic organic-inorganic hybrid materials to be higher than room temperature.