SnCo Nanoalloy/Graphene Anode Constructed by Microfluidic-Assisted Nanoprecipitation for Potassium-Ion Batteries
Guanjian Nie,Zhuonan Huang,Shukai Ding,Xiaodong Hao,Guoquan Suo,Di Han,Yang Xu,Yingjun Yang,Wenqi Zhao,Qingmei Su,Bingshe Xu,Gaohui Du,Christophe A. Serra
DOI: https://doi.org/10.1021/acsanm.1c04285
IF: 6.14
2022-02-09
ACS Applied Nano Materials
Abstract:Potassium-ion batteries have attracted substantial interest due to abundant resources and comparable electrochemical performance with lithium-ion batteries. Although plenty of graphene-based materials with ultrahigh performance have been designed, in practice, the dendrite growth induced by the capacitive-dominated potassium storage mechanism and the poor repeatability resulting from the complicated process are worrisome. To address these issues, it is envisaged that embedding SnCo nanoalloys in a graphene nanosheet matrix (SnCo NAs/G) can be an effective strategy for the following two reasons: (1) The embedded SnCo NAs are responsible for expanding the interlayer space and facilitating the potassium-ion diffusion in a graphene nanosheet matrix and (2) the combination of the microfluidic technology and the organic molecule confinement reaction endows the repeatability and large-scale production. As a result, the SnCo NAs/G-L anode is prepared with a low content of SnCo NAs (9.16 wt %). It shows advantages in the electrochemical performance as compared to the graphite anode. A reversible specific capacity of 165 mA h g–1 at 50 mA g–1 over 100 cycles is exhibited by SnCo NAs/G-L. It has a retention capacity of 179 mA h g–1, that is, 78.8% is recovered after charging at 500 mA g–1. Moreover, the intercalation reaction as the dominant potassium storage mechanism is beneficial for avoiding the safety problems arising from potassium dendrite growth. More interestingly, graphite-based composites constructed by the microfluidic technology successfully prove the high potential for large-scale production.
materials science, multidisciplinary,nanoscience & nanotechnology