Abstract:Utilizing electrodeposition technology, hydrogen evolution reaction catalytic electrodes, characterized by a multiscale rough surface structure, were developed on diverse conductive substrates, predominantly titanium mesh. This unique structure significantly curtailed bubble adhesion during hydrogen evolution, leading to a marked improvement in catalytic performance, notably surpassing that of commercial Pt plate, especially at high current densities. In response to the ongoing energy crisis, advancing the field of electrocatalytic water splitting is of utmost significance, necessitating the urgent development of high‐performance, cost‐effective, and durable hydrogen evolution reaction catalysts. But the generated gas bubble adherence to the electrode surface and sluggish separation contribute to significant energy loss, primarily due to the insufficient exposure of active sites, thus substantially hindering electrochemical performance. Here, we successfully developed a superaerophobic catalytic electrode by loading phosphorus‐doped nickel metal (NiPx) onto various conductive substrates via an electrodeposition method. The electrode exhibits a unique surface structure, characterized by prominent surface fissures, which not only exposes additional active sites but also endows the electrode with superaerophobic properties. The NiPx/Ti electrode demonstrates superior electrocatalytic activity for hydrogen evolution reaction, significantly outperforming a platinum plate, displaying an overpotential of mere 216 mV to achieve a current density of −500 mA cm−2 in 1 M KOH. Furthermore, the NiPx/Ti electrode manifests outstanding durability and robustness during continuous electrolysis, maintaining stability at a current density of −10 mA cm−2 over a duration of 2000 h. Owing to the straightforward and scalable preparation methods, this highly efficient and stable NiPx/Ti electrocatalyst offers a novel strategy for the development of industrial water electrolysis.

Catalysis of Hydrogen Evolution Reaction by Ni12P5 Single Crystalline Nanoplates and Spherical Nanoparticles

Boosting Electrocatalytic Activities of Pt-Based Mesoporous Nanoparticles for Overall Water Splitting by a Facile Ni, P Co-Incorporation Strategy

Heterostructured ZnIn2S4/Ni2P/NiS on Nickel Foam As Self-Supported Ph-All Electrocatalysts for Hydrogen Evolution

Hexagonal Nickel As a Highly Durable and Active Catalyst for Hydrogen Evolution

Sulfur-Doped Nickel Phosphide Nanoplates Arrays: A Monolithic Electrocatalyst for Efficient Hydrogen Evolution Reactions

Highly Efficient Water Splitting Catalyst Composed of N,P-Doped Porous Carbon Decorated with Surface P-Enriched Ni 2 P Nanoparticles

Colloid synthesis of Ni<sub>12</sub>P<sub>5</sub>/N, S-doped graphene as efficient bifunctional catalyst for alkaline hydrogen evolution and triiodide reduction reaction

Ni–C–N Nanosheets as Catalyst for Hydrogen Evolution Reaction

Regulating the Electronic Structure and Active Sites in Ni Nanoparticles by Coating N-Doped C Layer and Porous Structure for an Efficient Overall Water Splitting

Facile and Large-Scale Fabrication of Sub-3 Nm PtNi Nanoparticles Supported on Porous Carbon Sheet: A Bifunctional Material for the Hydrogen Evolution Reaction and Hydrogenation

Facile Synthesis of Well-Dispersed Ni2P on N-Doped Nanomesh Carbon Matrix as a High-Efficiency Electrocatalyst for Alkaline Hydrogen Evolution Reaction

Colloid synthesis of Ni 12 P 5 /N, S-doped graphene as efficient bifunctional catalyst for alkaline hydrogen evolution and triiodide reduction reaction

Monolithic Nickel Catalyst Featured with High‐Density Crystalline Steps for Stable Hydrogen Evolution at Large Current Density

Colloid synthesis of Ni12P5/N, S-doped graphene as efficient bifunctional catalyst for alkaline hydrogen evolution and triiodide reduction reaction

Surface-Engineered Ni(OH) 2 /PtNi Nanocubes as Cocatalysts for Photocatalytic Hydrogen Production

Optimizing Electrocatalytic Hydrogen Evolution Stability via Minimal Bubble Adhesion at Electrodeposited Crack‐Structured NiPx Catalysts

An efficient Ni3S2–Ni electrode constructed by a one-step powder metallurgy approach for the hydrogen evolution reaction

Surface engineering induced hierarchical porous Ni12P5-Ni2P polymorphs catalyst for efficient wide pH hydrogen production

Synthesis of NiMoO4/NiMo@NiS Nanorods for Efficient Hydrogen Evolution Reactions in Electrocatalysts

Modulating 3d Orbitals of Ni Atoms on Ni‐Pt Edge Sites Enables Highly‐Efficient Alkaline Hydrogen Evolution

Optimizing the activity of hydrogen evolution reaction through controllable synthesis of single crystal or polycrystalline Ni P