Stabilization of nano zero-valent iron by electrospun composite mat with good catalysis and recyclability
Yan Xu,Qi Guo,Yuan Li,Linjun Qin,Kegang Zhang,Guorui Liu,Chun-Gang Yuan
DOI: https://doi.org/10.1016/j.jclepro.2022.132459
IF: 11.1
2022-08-20
Journal of Cleaner Production
Abstract:Nano zero-valent iron (Fe0, nZVI) has been extensively utilized in the treatment of dyed wastewater. However, the dispersibility, stability and reusability of nZVI need to be improved for both efficiency and environmental safety. One nZVI modified nanofiber composite membrane was successfully fabricated by electrospinning, and the performances in different catalytic systems were evaluated. The synthesized composite mat was characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The loaded nZVI was verified by the change of fiber diameters and the distribution of iron element with/without loading. The composite membrane possessed good recyclability and dispersion property of nZVI with a mean diameter of 114.46 nm. Three Fenton-like oxidation systems (H2O2, Na2S2O8, and NaClO2) were selected and investigated for the degradation of Rhodamine B (RhB) in water using the as-prepared composite as a catalyzer. The degradability relationship of the oxidation systems was NaClO2>Na2S2O8>H2O2 with observed rate constants (Kobs) of 0.3155, 0.0547, and 0.014, respectively. 50 mg L−1 RhB was completely degraded by 1.5 mM NaClO2 in 15min, which is the best compared with the other two systems. The major free radical species (·OH, SO4·- and ClO2·) in the three oxidation systems were identified by electron paramagnetic resonance (EPR) and quenching studies. The degradation capacity could be maintained after five recycles and the leached nZVI from the composite was negligible (<0.55%). For the degradation process, the contribution of dark adsorption (Kads = 1.5489 × 10−3) was much smaller than that of natural-light-derived photocatalysis (Kphoto = 1.5489 × 10−3) with the adsorption capacity of 4.32 mg g−1 and oxidative degradation amounts of 9.46 mg g−1, 10.90 mg g−1 and 12.32 mg g−1 in H2O2, Na2S2O8 and NaClO2 systems, respectively. Our results demonstrated that the synthesized composite membrane demonstrated good catalytic properties with good recyclability and stability, and NaClO2 was the most efficacious system for RhB degradation in water.
environmental sciences,green & sustainable science & technology,engineering, environmental