Significantly Enhanced Photoluminescence and Thermal Stability of La3Si8N11O4:Ce3+,Tb3+ Via the Ce3+ → Tb3+ Energy Transfer: a Blue-Green Phosphor for Ultraviolet LEDs.

Hui-Bing Xu,Wei-Dong Zhuang,Rong-Hui Liu,Yuan-Hong Liu,Tian-Liang Zhou,Yujin Cho,Wei Gao,Chun-Pei Yan,Naoto Hirosaki,Rong-Jun Xie

DOI: https://doi.org/10.1039/c8ra07011c

IF: 4.036

2018-01-01

RSC Advances

Abstract:A series of Ce3+-, Tb3+- and Ce3+/Tb3+-doped La3Si8N11O4 phosphors were synthesized by gas-pressure sintering (GPS). The energy transfer between Ce3+ and Tb3+ occurred in the co-doped samples, leading to a tunable emission color from blue to green under the 360 nm excitation. The energy transfer mechanism was controlled by the dipole–dipole interaction. The Ce3+/Tb3+ co-doped sample had an external quantum efficiency of 46.7%, about 5.6 times higher than the Tb-doped La3Si8N11O4 phosphor (8.3%). The thermal quenching of the Tb3+ emission in La3Si8N11O4:Tb,Ce was greatly reduced from 74 to 30% at 250 °C, owing to the energy transfer from Ce3+ to Tb3+. The blue-green La3Si8N11O4:0.01Ce,0.05Tb phosphor was testified to fabricate a warm white LED that showed a high color rendering index of 90.2 and a correlated color temperature of 3570 K. The results suggested that the co-doped La3Si8N11O4:Ce,Tb phosphor could be a potential blue-green down-conversion luminescent material for use in UV-LED pumped wLEDs.