Efficient 2 Μm Emission in Er3+/Ho3+ Co-Doped Lead Silicate Glasses under Different Excitations
Guoquan Qian,Guowu Tang,Zhenguo Shi,Licheng Jiang,Kaimin Huang,Jiulin Gan,Dongdan Chen,Qi Qian,Feng Tu,Haizheng Tao,Zhongmin Yang
DOI: https://doi.org/10.1016/j.optmat.2018.05.061
IF: 3.754
2018-01-01
Optical Materials
Abstract:Er3+ has been considered one of the most suitable sensitive ions of Ho3+ to generate 2 mu m emission. In this work, luminescent properties and energy transfer mechanism of Er3+/Ho3+ co-doped lead silicate glass were systematically investigated under 980 and 1550 run excitations, respectively. Based on the absorption spectra, the Judd-Ofelt intensity parameters, absorption and emission cross sections, and gain coefficient were calculated. The emission cross section of Ho3+: I-5(7) -> I-5(8) transition is as large as 8 x 10(-21) cm(2). And the calculated maximum gain coefficient is 3.48 cm(-1) at 2010 nm. In addition, the energy transfer efficiency between Er3+: I-4(13/2) level and Ho3+: I-5(7) level can reach 89.3% when the samples were pumped by a 980 nm laser diode. An intense 2 mu m emission was obtained upon excitation of 1550 nm due to the large absorption cross section of Er3+ at 1550 nm and efficient energy transfer from Er3+: I-4(13/2) level to Ho3+: I-5(7) level. These results suggest that the Er3+/Ho3+ co-doped lead silicate glass has great potential for application as a mid-infrared laser material.