Abstract:As a toxic pollutant, carbon monoxide (CO) usually causes harmful effects on human health. Therefore, the thermally catalytic oxidation of CO has received extensive attention in recent years. The CuO-based catalysts have been widely investigated due to their availability. In this study, a series of transition metal oxides (Fe2O3, Co3O4 and NiO) promoted CuO-based catalysts supported on the α-MnO2 nanowire catalysts were prepared by the deposition precipitation method for catalytic CO oxidation reactions. The effects of the loaded transition metal type, the loading amount, and the calcination temperature on the catalytic performances were systematically investigated. Further catalyst characterization showed that the CuO/α-MnO2 catalyst modified with 3 wt% Co3O4 and calcined at 400 °C performed the highest CO catalytic activity (T90 = 75 °C) among the investigated catalysts. It was supposed that the loading of the Co3O4 dopant not only increased the content of oxygen vacancies in the catalyst but also increased the specific surface area and pore volume of the CuO/α-MnO2 nanowire catalyst, which would further enhance the catalytic activity. The CuO/α-MnO2 catalyst modified with 3 wt% NiO and calcined at 400 °C exhibited the highest surface adsorbed oxygen content and the best normalized reaction rate, but the specific surface area limited its activity. Therefore, the appropriate loading of the Co3O4 modifier could greatly enhance the activity of CuO/α-MnO2. This research could provide a reference method for constructing efficient low-temperature CO oxidation catalysts.

Cu2O–CuO Hollow Nanospheres As a Heterogeneous Catalyst for Synergetic Oxidation of CO

Large-scale Synthesis and Catalytic Activity of Nanoporous Cu–O System Towards CO Oxidation

Site‐Resolved Cu2O Catalysis in the Oxidation of CO

CO Oxidation over the Cu2O/CuO Hollow Sphere Heterojunction Catalysts with Enhanced Low-Temperature Activities

Fabricating Cu2O-CuO Submicron-Cubes for Efficient Catalytic CO Oxidation: the Significant Effect of Heterojunction Interface

Designing Highly Efficient Cu2O-CuO Heterojunction CO Oxidation Catalysts: the Roles of the Support Type and Cu2O-CuO Interface Effect

Decoration of CeO 2 Nanoparticles on Cu/Co Bimetallic Oxide and Their Catalytic Performance

Hetero-metal Cation Control of CuO Nanostructures and Their High Catalytic Performance for CO Oxidation.

Solid-State Construction of CuOx/Cu1.5Mn1.5O4 Nanocomposite with Abundant Surface CuOx Species and Oxygen Vacancies to Promote CO Oxidation Activity

Interfacial electron modulation of Cu2O by Co3O4 embedded in hollow carbon cube skeleton for boosting oxygen reduction/revolution reactions

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

CuO/TiO 2 /Ti Monolithic Catalysts for Low-Temperature CO Oxidation

Facile synthesis of well-dispersed CeO2–CuOx composite hollow spheres with superior catalytic activity for CO oxidation

Mechanistic study of low-temperature CO oxidation over CuO/Cu2O interfaces with oxygen vacancy modification

Cu2O nanocubes with mixed oxidation-state facets for (photo)catalytic hydrogenation of carbon dioxide

Enhancing the Low-Temperature CO Oxidation over CuO-Based -MnO<sub>2</sub> Nanowire Catalysts

Hollow-Structural Ag/Co3O4 Nanocatalyst for CO Oxidation: Interfacial Synergistic Effect

Constructing Efficient CuO-Based CO Oxidation Catalysts with Large Specific Surface Area Mesoporous CeO2 Nanosphere Support

Sheet-Like Morphology CuO/Co3O4 Nanocomposites for Enhanced Catalysis in Hydrogenation of CO2 to Methanol

Interfacial Cu+ promoted surface reactivity: Carbon monoxide oxidation reaction over polycrystalline copper–titania catalysts

CeO2 nanoparticles modified by CuO nanoparticles for low-temperature CO oxidation with high catalytic activity