In Situ Generated Carbon Nanosheet-Covered Micron-Sized Porous Si Composite for Long-Cycling Life Lithium-Ion Batteries
Wen Luo,Chenhui Fang,Xiaofeng Zhang,Jiaxing Liu,Hong Ma,Guoqing Zhang,Zhongyun Liu,Xinxi Li
DOI: https://doi.org/10.1021/acsaem.0c02445
IF: 6.4
2020-12-24
ACS Applied Energy Materials
Abstract:Micron-sized silicon-based materials have attracted immense attention for large-scale lithium-ion batteries (LIBs) owing to high theoretical capacity and low cost. However, it is limited by severe volume expansion and fast capacity fading in a cycling process. Here, we proposed a facile strategy to obtain an in situ formed carbon nanosheet template-covered micron-sized porous silicon composite () from the low-cost Al–Si alloy and bicontinuous C<sub>6</sub>H<sub>12</sub>O<sub>6</sub>/SiO<sub>2</sub> structural layer. The templated assembly of the inner distributed PSi and outer in situ generated CNS can form a stable and controllable conductive structure with an increased specific surface area and enhanced intermolecular interactions. This unique composite structure results in a significant increase of electrolyte transfer and long-term stability. As an anode material for LIBs, the composite exhibits a high reversible capacity of 1272 mA h g<sup>–1</sup> at 1 A g<sup>–1</sup> after 500 cycles in the micron-sized PSi/C composite system. This work provides a templated idea for long-term stable LIBs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c02445?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c02445</a>.Long-term cycling performance of three samples of different proportions at a current of 0.5 A g<sup>–1</sup>; long-term cycling performance of three samples of different proportions at a current of 1 A g<sup>–1</sup>; Si 2p XPS spectra of PSi, <sub>6</sub>H<sub>12</sub>O<sub>6</sub>/SiO<sub>2</sub>, /SiO<sub>2</sub>, and ; high-resolution C 1s XPS spectra of ; TGA curve of ; SEM images of Al–Si spheres; SEM images of at low magnifications; elemental mappings of ; HRTEM and lattice of ; EIS of PSi and /SiO<sub>2</sub> and PSi; plot <i>Z</i>′ versus ω<sup>–1/2</sup> of PSi, /SiO<sub>2</sub> and at a low frequency; cross-sectional SEM image of the PSi, /SiO<sub>2</sub>, and samples before and after 500 cycles at a current density of 1 A g<sup>–1</sup>; pore volume, pore size, and specific surface area of PSi and <sub>6</sub>H<sub>12</sub>O<sub>6</sub>/SiO<sub>2</sub>, /SiO<sub>2</sub>, and ; and equations of the Li + diffusion coefficient (<i>D</i>) (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c02445/suppl_file/ae0c02445_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels