Negative Lattice Expansion induced Upconversion Luminescence Thermal Enhancement in novel Na2MoO4:Yb3+, Er3+ Transparent Glass Ceramics towards Temperature Sensing Application
Yingzhu Zi,Yangke Cun,Xue Bai,Zan Xu,Asif Ali Haider,Jianbei Qiu,Zhiguo Song,Anjun Huang,Jialun Zhu,Zhengwen Yang
DOI: https://doi.org/10.1039/d2tc05009a
IF: 6.4
2022-12-24
Journal of Materials Chemistry C
Abstract:Negative lattice expansion induced upconversion luminescence thermal enhancement is an efficient way to solve the problems of thermal quenching of lanthanides ions, which could be combined with traditional fluorescence intensity ratio technology to obtain temperature-sensing characteristic. In this work, linear negative lattice thermal expansion Na2MoO4:Yb3+, Er3+ transparent glass-ceramics were fabricated by a low temperature co-sintering approach. Thermal enhancement of UCL at 525 and 806/860 nm of the glass ceramics is caused by the increase of energy transfer between Yb3+ and Er3+ ions induce by the linear negative thermal expansion properties of orthorhombic Na2MoO4 nanoparticles. Combining the upconversion luminescence characteristics of positive thermal expansion tellurite glass matrix and negative thermal expansion Na2MoO4:Yb3+, Er3+ nanoparticles, a novel glass ceramic temperature sensor was obtained. The temperature relative sensitivity was manipulated by selecting different UCL spectral modes, which is up to 3.14 %K-1 (313 K), showing better performance than many glass ceramics reported previously. The cycle measurement of UCL response alternating between 313 and 573 K presents excellent repeatability, exhibiting the potential application of Na2MoO4: Yb3+, Er3+ transparent glass ceramics as a new generation temperature sensor.
materials science, multidisciplinary,physics, applied