Abstract:A hard carbon material with free-standing porous structure and high contents of heteroatom functional groups is considered to be a potential anode for potassium-ion batteries (PIBs). Herein, a free-standing phosphorus/nitrogen cofunctionalized porous carbon monolith (denoted as PN-PCM) anode for PIBs is successfully fabricated via a supercritical CO2 foaming technology, followed by amidoximation, phosphorylation, and thermal treatment. Thanks to the synergistic effect of a three-dimensional macroporous open structure and high P/N contents of 6.19/5.74 at%, the PN-PCM anode delivers an excellent reversible specific capacity (396 mA h g–1 at 0.1 A g–1 after 300 cycles) with high initial Coulombic efficiency (63.6%), a great rate performance (168 mA h g–1 at 5 A g–1), and an ultralong cycling stability (218 mA h g–1 at 1 A g–1 after 3000 cycles). Theoretical calculations clarify that in a P/N cofunctionalized carbon, the P–C bonds devote more to enhancing the potassium storage via adsorption and improving electronic conductivity of carbon, while P–O bonds contribute more to enlarging the interlayer distance of carbon and reducing the ion diffusion barrier.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c06690?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c06690</a>.SEM images of PAN/PMMA foam and N-PCM. TEM images, SAED pattern, and TEM elemental distribution mapping images of N-PCM. TEM images and the corresponding pore diameter distributions of PN-PCM and N-PCM. Carbon dioxide adsorption isotherms and the corresponding micropore size distributions of PN-PCM and N-PCM. High-resolution N 1s, O 1s, and C 1s spectra of N-PCM, PN-PCM-L, PN-PCM, and PN-PCM-H. FTIR spectra of PN-PCM, N-PCM, PA-PAN, and PAN. Rate performances of N-PCMs carbonized at different temperatures, PN-PCMs prepared using different phosphoric acid concentrations, and PN-PCMs carbonized at different temperatures. EIS measurements of PN-PCM and N-PCM. Digital photographs and SEM images of PN-PCM and N-PCM after 3000 cycles. GITT profiles and the corresponding diffusion coefficients of the charge process of PN-PCM and N-PCM. Structure models of different carbon structures. Interlayer distances measured at different positions of various carbon structures before and after insertion of potassium ions. Elemental analysis of N-PCM, PN-PCM-L, PN-PCM, and PN-PCM-H. Electrochemical performances of recently reported carbon anodes for PIBs (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c06690/suppl_file/nn0c06690_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Insights into the Na+ Storage Mechanism of Phosphorus‐Functionalized Hard Carbon As Ultrahigh Capacity Anodes

Biomass‐Derived Phosphorus‐Doped Porous Hard Carbon Anode for Stable and High‐Rate Sodium Ion Batteries

Regulate Phosphorus Configuration in High P-Doped Hard Carbon as a Superanode for Sodium Storage

Nitrogen/Phosphorus Dual‐Doped Hard Carbon Anode with High Initial Coulombic Efficiency for Superior Sodium Storage

Ultrahigh Phosphorus Doping of Carbon for High‐Rate Sodium Ion Batteries Anode

Unveiling the Interfacial Instability of the Phosphorus/Carbon Anode for Sodium-Ion Batteries

Well-dispersed Phosphorus Nanocrystals Within Carbon Via High-Energy Mechanical Milling for High Performance Lithium Storage

P-doped hard carbon material for anode of sodium ion battery was prepared by using polyphosphoric acid modified petroleum asphalt as precursor

Sulfur and phosphorus co-doped hard carbon derived from oak seeds enabled reversible sodium spheres filling and plating for ultra-stable sodium storage

Nano-confining Red Phosphorus in a Carbon Hierarchical Superstructure for Superior Potassium Storage

Nanoconfining red phosphorus within MOF-derived hierarchically porous carbon networks for high performance potassium storage

Constructing high-rate and long-life phosphorus/carbon anodes for potassium-ion batteries through rational nanoconfinement

Nitrogen and phosphorus co-doped hard carbon materials as high-performance anode for sodium ion batteries

Nitrogen/phosphorus co-doped ultramicropores hard carbon spheres for rapid sodium storage

Superior Sodium Storage in Phosphorus@porous Multichannel Flexible Freestanding Carbon Nanofibers

Understanding of the Capacity Contribution of Carbon in Phosphorus-Carbon Composites for High-Performance Anodes in Lithium Ion Batteries

Spatially confining and chemically bonding amorphous red phosphorus in the nitrogen doped porous carbon tubes leading to superior sodium storage performance

Tailoring Conductive Networks Within Hollow Carbon Nanospheres to Host Phosphorus for Advanced Sodium Ion Batteries

Controllable Phosphorylation Strategy for Free-Standing Phosphorus/Nitrogen Cofunctionalized Porous Carbon Monoliths as High-Performance Potassium Ion Battery Anodes

In Situ Revealing the Electroactivity of P ? O and P ? C Bonds in Hard Carbon for High‐Capacity and Long‐Life Li/K‐Ion Batteries

P-doped spherical hard carbon with high initial coulombic efficiency and enhanced capacity for sodium ion batteries