Abstract:We present a general, convenient, and efficient synthetic concept for the coating of colloidal particles with a silica (SiO2) shell of well-defined and precisely controlled morphology and porosity. Monodisperse submicroscopic polystyrene (PS) particles were synthesized via two-stage emulsifier-free emulsion polymerization and subsequent swelling polymerization, enabling selective particle surface modification by the incorporation of ionic (methacrylic acid, MAA) or nonionic (hydroxyethyl methacrylate, HEMA or methacrylamide, MAAm) comonomers, which could be proven by zeta potential measurements as well as by determining the three-phase contact angle of the colloidal particles adsorbed at the air-water and n-decane-water interface. The functionalized particles could be directly coated with silica shells of variable thickness, porosity, and controlled surface roughness in a seeded sol gel process from tetraethoxysilane (TEOS), leading to hybrid PS@silica particles with morphologies ranging from core-shell (CS) to raspberry-type architectures. The experimental results demonstrated that the silica coating could be precisely tailored by the type of surface functionalization, which strongly influences the surface properties of the colloidal particles and thus the morphology of the final silica shell. Furthermore, the PS cores could be easily removed by thermal treatment, yielding extremely uniform hollow silica particles, while maintaining their initial shell architecture. These particles are highly stable against irreversible aggregation and could be readily dried, purified, and redispersed in various solvents. Herein we show a first example of coating semiconducting CdSe/ZnS nanocrystals with smooth and spherical silica shells by applying the presented method that are expected to be suitable systems for applications as markers in biology and life science by using fluorescence microscopy methods, which are also briefly discussed.

One-pot Formation of Monodisperse Polymer@sio2 Core–shell Nanoparticles Via Surfactant-Free Emulsion Polymerization Using an Adaptive Silica Precursor Polymer

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Preparation Of Monodisperse Silica/Pmma Core/Shell Nanoparticles With Controllable Shell Thickness By Soap-Free Emulsion Polymerization

Synthesis of organic-inorganic hybrid core-shell nanoparticles and particle size control

Preparation of SiO2/PMMA Composite Particles Via Conventional Emulsion Polymerization

Synthesis of SiO2/Polystyrene Nanocomposite Particles Via Miniemulsion Polymerization

Preparation of Highly Monodisperse Hybrid Silica Nanospheres Using a One-Step Emulsion Reaction in Aqueous Solution

Formation of Monodispersed Polymer Particles in Emulsifier-Free Emulsion Polymerization

Novel Polymeric Organosilica Precursor and Emulsion Stabilizer: Toward Highly Elastic Hollow Organosilica Nanospheres.

Formation of Novel Polymeric Nanoparticles.

Preparation and Morphology of SiO 2 /PMMA Nanohybrids by Microemulsion Polymerization

One-Step Preparation of Both Micron and Nanoparticles

One-Pot Preparation of Hollow Silica Spheres by Using Thermosensitive Poly(N-Isopropylacrylamide) As A Reversible Template

Emulsion droplets as a dynamic interface for the direct and large-scale synthesis of ultrathin free-standing mesoporous silica films as well as 2D polymeric and carbon nanomaterials.

Biomimic preparation of highly dispersible silica nanoparticles based polymer nanocomposites

Formation of Novel Polymeric

Morphology-Controlled Coating of Colloidal Particles with Silica: Influence of Particle Surface Functionalization

In Situ Formation of Silica Nanoparticles Decorated with Well-Defined Homopolymers and Block Copolymers

Synthesis of Raspberry‐like Silica/polystyrene/silica Multilayer Hybrid Particles Via Miniemulsion Polymerization

A non-surfactant self-templating strategy for mesoporous silica nanospheres: beyond the Stöber method

Preparation of core-shell nanoparticles <i>via</i> emulsion polymerization induced self-assembly using a maleamic acid--methyl styrene copolymer as a macro-initisurf