Abstract:In this paper, We prepared two groups of the glasses, the first group is Ge x As 20 Se 80-x with x from 5 % to 32.5 %, the second group is Ge x Sb 20 Se 80-x with x from 5 % to 25 %, using the conventional melt-quench method, and investigated the effect of the elemental substitution of As by Sb on the threshold behaviors in Ge x As(Sb) 20 Se 80-x glasses. We aimed to understand that,to which degree the topological model and chemical order model can explain the correlation between the physical properties and glass compositions, and how the chemical composition can affect the transition threshold in the glasses. Glass transition temperature was measured by the differential scanning calorimeter (Mettler-Toledo, DSC1) with different scanning rates from 5 K/min to 30 K/min under a uniform nitrogen gas flow of 50 mL/min, the density of the glasses was measured by a Mettler H20 balance with a MgO crystal used as a reference. Samples from each glass composition were weighed five times and the average density was recorded, the refractive index of the glass at 1.5 um was measured by a Metricon Model 2010 prism coupler. Raman spectra were measured from a T64000 Jobin-Yvon-Horiba micro-Raman spectrometer equipped with a liquid-nitrogen-cooled CCD detector. The 830 nm laser line was used as an excitation source, and the laser power was kept as small as possible to avoid any photo-induced effects. The resolution of the spectrometer was about 0.5 cm -1 . The result from systematic measurements of these physical parameters shows that, while the transition thresholds at MCN=2.4 and 2.67 were verified in the Ge-As-Se glasses with ideal covalent network, these two transitions represent the covalent network structure inside the glass from an under-constrained “floppy” network to an over-constrained “rigid” phase and from the two-dimensional to the three-dimensional “stressed rigid” phase respectively. However, when As is substituted by Sb, the Ge x Sb 20 Se 80-x glass with non-ideal covalent network will change of the transition thresholds, which changes to the chemically stoichiometric composition. We further deconvolved Raman scattering spectra into different structural units and the change of their respective intensity showed the same behavior, and this was ascribed to the chemical effect induced by a large difference of the atomic radius between As and Sb, and a relatively strong ionic feature of the element Sb.

The Onset Temperature (tg) of As Se1 Glasses Transition Prediction: A Comparison of Topological and Regression Analysis Methods

Effect of the elemental substitution on threshold behaviours in Ge-As(Sb)-Se glasses

A combinatorial machine-learning-driven approach for predicting glass transition temperature based on numerous molecular descriptors

Visual analytics of an interpretable prediction model for the glass transition temperature of fluoroelastomers

A Simple and Sensitive Method for an Important Physical Parameter: Reliable Measurement of Glass Transition Temperature by AIEgens

Prediction and Interpretability Study of the Glass Transition Temperature of Polyimide Based on Machine Learning with Quantitative Structure-Property Relationship (Tg-QSPR)

Shallow neural networks to predict glass transition, crystallization and liquidus temperature of iron-based metallic glasses

Efficient Prediction of Polymer Glass Transition Temperatures through Machine Learning Methods

Intermediate phase, network demixing, boson and floppy modes, and compositional trends in glass transition temperatures of binary AsxS1-x system

Quantitative structure-property relationship of glass transition temperatures for organic compounds

A neural network approach to prediction of glass transition temperature of polymers

Ridge regression for predicting elastic moduli and hardness of calcium aluminosilicate glasses

Self-supervised Learning for Glass Property Screening

Consistent and reproducible computation of the glass transition temperature from molecular dynamics simulations

Quick and accurate optical thermometry based on chemometrics model strategy in Na0.5Gd0.5TiO3: Er3+

Modified Group Contribution Scheme to Predict the Glass-Transition Temperature of Homopolymers through a Limiting Property Dataset

Rigidity theory of glass: Determining the onset temperature of topological constraints by molecular dynamics

Thermal properties of chalcogenide glasses in the GeSe2–As2Se3–CdSe system

Machine learning analysis of a large set of homopolymers to predict glass transition temperatures

The proper glass transition temperature of amorphous polymers on dynamic mechanical spectra

A Quantitative Structure-Property Relationship Study of the Glass Transition Temperature of OLED Materials.