Abstract:Catalytic decomposition of benzene was studied by using oxides of vanadium and tungsten supported on titanium oxide (TiO2) catalysts for effective reduction of emissions of toxic organic compounds from waste incineration. Experiments were conducted to evaluate the effects of the catalyst's composition, and operating conditions on benzene decomposition, and the relationship between molecular structures of catalysts and their activity was also investigated through replacing the conventional TiO2 catalyst support by nano-sized TiO2. Trace levels (1 and 10 ppm) of gaseous benzene were catalytically decomposed in a fixed-bed catalytic reactor with monolithic oxides of vanadium and tungsten supported on titanium oxide (V2O5-WO3/TiO2) catalysts under conditions simulating the cooling of waste incineration flue gas. On-line monitoring of trace benzene concentrations before and after the catalyst was achieved by means of resonance enhanced multiphoton ionization-time of flight mass spectrometry (REMPI-TOFMS). Catalysts were characterized by nitrogen adsorption, X-ray diffraction, energy dispersive X-ray spectroscopy, temperature-programmed reduction, and Raman spectroscopy. The effects of several parameters, including catalyst operating temperature, space velocity (SV) and initial benzene concentration, on catalytic oxidation of benzene were investigated. Experimental results indicate that reduction of the initial benzene concentration from 10 to 1 ppm either enhances or decreases the catalytic removal efficiency depending on the adsorption capability as well as the oxidation ability of the catalyst tested. The catalytic activity for benzene oxidation not simply relies on the vanadium content of the catalyst; the molecular structure of vanadium oxide, which is known to be influenced by both vanadium oxide loading and the type of support, is very important. Nano-sized TiO2 supported vanadium oxide catalyst (VWNT) with lowest V loading (0.75 wt.%) provides higher catalytic activity than those of the catalysts with higher V contents (1.31 and 2.92 wt.%) but supported by conventional TiO2 (VWT1 and VWT2). The relatively higher catalytic activity of VWNT may be attributed to: (a) the presence of monomeric VOx species, with one terminal V=O bond as indicated by Raman spectra; (b) fewer impurities confounding active catalytic constituents (V, W and Ti); (c) pure anatase phase of TiO2 rather than a mixture phase of anatase and rutile servicing as catalyst support besides its nano-scale particle size; (d) larger specific surface area, smaller average pore diameter, and narrower pore size distribution contribute higher adsorption ability for benzene. No obvious competition effect between NOx removal and benzene oxidation was observed in this study. Reaction rate constants and activation energies for benzene catalytic oxidation tested by the catalysts were calculated. Lower activation energy obtained from VWNT than those of the two catalysts further confirming the higher catalytic activity of VWNT. Published by Elsevier B.V.

BiVO4/α-Fe2O3 Catalytic Degradation of Gaseous Benzene: Preparation, Characterization and Photocatalytic Properties

BiVO4/TiO2 Nanocrystalline Heterostructure: A Wide Spectrum Responsive Photocatalyst Towards the Highly Efficient Decomposition of Gaseous Benzene

Hydrothermal synthesis of BiVO 4 /TiO 2 composites and their application for degradation of gaseous benzene under visible light irradiation

Robust Photocatalytic Performance of Tio2/Bi2wo6 Photocatalysts with Trace Fe Dopant for Gaseous Toluene Decomposition

Study on the Decomposition of Trace Benzene over V2O5–WO3/TiO2-based Catalysts in Simulated Flue Gas

Fe2O3/BiVO4 heterogeneous photo-Fenton catalyst with excellent dye degradation performance prepared by ultrasonic-assisted calcination

Highly Efficient Oxidation Of Gaseous Benzene On Novel Ag3vo4/Tio2 Nanocomposite Photocatalysts Under Visible And Simulated Solar Light Irradiation

Photocatalytic Degradation of Gaseous Benzene Using Cu/Fe-Doped TiO2 Nanocatalysts under Visible Light

Positive effect of Fe3+ ions on Bi2WO6, Bi2MoO6 and BiVO4 photocatalysis for phenol oxidation under visible light

Mesoporous TiO2 under VUV Irradiation: Enhanced Photocatalytic Oxidation for VOCs Degradation at Room Temperature

Facile Assembly of InVO4/TiO2 Heterojunction for Enhanced Photo-Oxidation of Benzyl Alcohol

CuCoOx/BiVO4 Multifunctional Catalyst for Organics Degradation, Water Oxidation, and O2 Reduction under Visible Light

A Novel Step-Scheme BiVO4/Ag3VO4 Photocatalyst for Enhanced Photocatalytic Degradation Activity under Visible Light Irradiation

Improved Performance of BiVO4 via a Surface Deposited Magnetic CuFe2O4 for Phenol Oxidation, O2 Reduction and Evolution under Visible Light.

Preparation and Visible Light Catalytic Performance of Fe3O4/Ag/BiVO4/Sepiolite Composites

Enhanced photocatalytic degradation of methylene blue through synthesizing of novel of BiVO4/Zn2SnO4 under visible light

Synthesis of Visible-Light Sensitive M–BiVO4 (m=ag, Co, and Ni) for the Photocatalytic Degradation of Organic Pollutants

BiVO 4 /G-C 3 N 4 Composite Visible-Light Photocatalyst for Effective Elimination of Aqueous Organic Pollutants

Structural characterization and photocatalytic properties of novel Bi<sub>2</sub>FeVO<sub>7</sub>

Preparation and photocatalytic properties of Ag/BiVO4/BiPO4 heterojunction nanofibers

Photocatalytic performance of TiO2/Bi2WO6 photocatalysts with trace Fe3+ dopant for gaseous toluene decomposition