Abstract:In this study, a novel technique of consecutive multi-pass cooperative lowered-temperature rolling (CMCLR) was proposed for the first time, with the purpose of preparing high performance wrought magnesium alloys. Based on this, a highly ductile magnesium alloy sheet could be effectively produced from ingot. The corresponding microstructure could directly evolve from coarse dendrites to equiaxed grains with an average size of similar to 5 mu m, which was attributed to the intense dynamic recrystallization (DRX) during isothermal deformation. The equivalent strain gradually decreased from the surface to the interior and edge of the rolled sheet due to the anisotropic plastic deformation. Instead, the temperature of the core of the sheet was slightly higher than that of the surface due to the deformation heat effect. The basal texture in the RD-TD plane generally weakened in the form of the splitting of basal texture toward the RD and the broadening of basal plane away from the pole center due to texture randomization dominated by DRXed grains. The exceptional ductility of more than 28.7% together with acceptable ultimate tensile strength of not less than 267 MPa was ascribed to the progressive work hardening as a result of seamless switching of multiple deformation modes, i.e., basal dislocation-slip-mediated deformation was preferentially operated and then was substituted by twinning-controlled deformation and non-basal dislocation-slip-dominated deformation. The selection of {10 (1) over bar2} twin variants agreed well with geometrical compatibility factor (m') criterion instead of Schmid's law. The activated twin variants nearly engulfed the whole parent grains for the sake of preserving compatible deformation continuity at ambient temperature, giving rise to the formation of TD-split texture. Comparatively, the {10 (1) over bar2} twinning could randomize the basal texture via reorienting grain orientations which in turn facilitated the reactivation of dislocation slip systems in the case of high temperature deformation.

Prominent Role of a High Volume Fraction of Mg17Al12 Particles on Tensile Behaviors of Rolled Mg–Al–Zn Alloys

Prominent Role of High-Volume Fraction Mg17Al12 Dynamic Precipitations on Multimodal Microstructure Formation and Strength-Ductility Synergy of Mg–Al–Zn Alloys Processed by Hard-Plate Rolling (HPR)

Development of a Novel Strength Ductile Mg–7Al–5Zn Alloy with High Superplasticity Processed by Hard-Plate Rolling (HPR)

Superplastic Deformation Behavior of Rolled Mg-8Al-2Sn and Mg-8Al-1Sn-1Zn Alloys at High Temperatures

Realizing impressive superplasticity in a low-alloyed Mg-Zn-Ca-Al-Mn alloy: The roles of grain boundary segregation and dense β-Mn particles

Achieving Bimodal Microstructure and Enhanced Tensile Properties of Mg–9Al–1Zn Alloy by Tailoring Deformation Temperature During Hard Plate Rolling (HPR)

Development of Mg–6Al–4Sn–1Zn Alloy Sheets with Ultra-High Strength by Combining Extrusion and High-Speed Rolling

Effect of Tensile Direction on Mechanical Properties and Microstructural Evolutions of Rolled Mg-Al-Zn-Sn Magnesium Alloy Sheets at Room and Elevated Temperatures

On Mechanical Properties and Superplasticity of Mg–15Al–1Zn Alloys Processed by Reciprocating Extrusion

A superplastic bimodal grain-structured Mg–9Al–1Zn alloy processed by short-process hard-plate rolling

Achieving Fine Grain Structure and Superplasticity in AZ91-0.4Sn Magnesium Alloy Using Short Flow Rolling Process

Developing High-Strength and Ductile Mg-Gd-Y-Zn-Zr Alloy Sheet Via Bimodal Grain Structure Coupling with Heterogeneously-Distributed Precipitates

Excellent High Strain Rate Superplasticity of Al-Mg-Sc-Zr Alloy Sheet Produced by an Improved Asymmetrical Rolling Process

A Comparison of Microstructure and Mechanical Properties of Mg–9Al–1Zn Sheets Rolled from As-Cast, Cast-Rolling and As-Extruded Alloys

Microstructure and Tensile Properties of Rolled Mg-4Al-2Sn-1Zn Alloy with Pre-Rolling Deformation

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

Effect of Large Thickness-Reduction on Microstructure Evolution and Tensile Properties of Mg-9Al-1Zn Alloy Processed by Hard-Plate Rolling

An Exceptional Ductility of AZ31 Magnesium Alloy Sheet Achieved by Consecutive Multi-Pass Cooperative Lowered-Temperature Rolling

Achieving Superplasticity in AZ31 Magnesium Alloy Processed by Hot Extrusion and Rolling

Achieving Exceptionally High Strength in Mg3Al1Zn-0.3Mn Extrusions Via Suppressing Intergranular Deformation

Achieving ultrahigh strength in binary Al-10Mg alloy through heavy cryogenic rolling