Ho‐doped SrBi2Nb2O9 multifunctional ceramics with bright green emission and good electrical properties

Lei Yu,Jigong Hao,Zhijun Xu,Wei Li,Ruiqing Chu

DOI: https://doi.org/10.1002/pssa.201700276

2017-01-01

Abstract:Ho3+-doped SrBi2Nb2O9 multifunctional ferroelectric ceramics with bright green light emission and good electrical properties were fabricated in this work. Under blue light excitation, samples showed bright green light with two typical emission bands: a strong green emission centered at 545nm corresponding to the intra f-f transition from the excited S-5(2) to the ground state I-5(8) and a relatively weak red emission located 653nm induced by the (F5I8)-F-5-I-5 transition of Ho3+. Due to the concentration quenching effect, the intensity of emission was strongly dependent on the doping concentration. Furthermore, the electrical properties have improved by Ho3+ doping. At x=0.004, samples exhibit optimal electrical properties with high Curie temperature (T-c=441 degrees C) and large 2P(r) and d(33) values (2P(r)=15.54 mu Ccm(-2), d(33)=19 pC/N). These results demonstrate that the SBN-xHo ceramics possess excellent multifunctional properties to achieve a variety of applications.