ZIF-67-templated synthesis of core-shell-structured POP@MOF composite derived porous carbon with embedding FeCo alloy nanoparticles as high-performance bifunctional oxygen electrocatalysts
Meng Zhang,Fang Yan,Jingkun Bai,Xiaotong Li,Xiao Zheng,Jinli Dou,Xuedong Wang,Weifen Zhang,Baolong Zhou
DOI: https://doi.org/10.1016/j.micromeso.2020.110627
IF: 5.876
2021-01-01
Microporous and Mesoporous Materials
Abstract:<p>Herein, Fe-phthalocyanine-based conjugated microporous polymer (Fe-Phth-CMP) coated metal organic framework (ZIF-67) composites, namely , were facilely prepared via a rational and effective solid-phase synthesis method, in which, ZIF-67 worked as both precursors and templates. Upon carbonization, these special composites, with controllable morphology similar to ZIF-67 and adjustable Fe/Co molar ratio, can be further converted into N-doped porous carbons embedded with highly dispersed FeCo alloy and Fe/Co–N active sites. The optimal catalyst (denoted as P<sub>2</sub>Z<sub>3</sub>-900, prepared in a mass ratio of m<sub>POP</sub>: m<sub>ZIF</sub> = 2 : 3) features hierarchical pore structure which could significantly enhance the mass transfer efficiency and promotes the exposure of active sites, leading to high ORR and OER activity in alkaline conditions, simultaneously. For example, P<sub>2</sub>Z<sub>3</sub>-900 presents a half-wave potential (E<sub>1/2</sub>) of 0.81 V (vs RHE) with a diffusion-limited current density of 5.56 mA cm<sup>−2</sup>, comparable to commercial Pt/C (0.83 V and 5.60 mA cm<sup>−2</sup>), but much better than other prepared control samples. The <em>Eonset</em> of OER at 10 mA cm<sup>−2</sup> reaches 1.60 V with a small Tafel slope of 57 mV dec<sup>−1</sup>. More importantly, the current synthetic method offers a rational strategy to structure-, morphology-, and element composition-controlled porous carbons, thereby finely regulating the property for efficient catalysis.</p>
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied