Dielectric Response and Percolation Behavior of Ni–P(VDF–TrFE) Nanocomposites

Lin Zhang,Patrick Bass,Guan Wang,Yang Tong,Zhuo Xu,Z. -Y. Cheng

DOI: https://doi.org/10.1142/s2010135x17500151

2017-01-01

Journal of Advanced Dielectrics

Abstract:Conductor–dielectric 0–3 nanocomposites using spherical nickel nanoparticles as filler and poly(vinylidene fluoride–trifluoroethylene) 70/30[Formula: see text]mol.% as matrix are prepared using a newly developed process that combines a solution cast and a hot-pressing method with a unique configuration and creates a uniform microstructure in the composites. The uniform microstructure results in a high percolation threshold [Formula: see text] ([Formula: see text] vol.%). The dielectric properties of the nanocomposites at different frequencies over a temperature range from [Formula: see text]70[Formula: see text]C to 135[Formula: see text]C are studied. The results indicate that the composites exhibit a lower electrical conductivity than the polymer matrix. It is found that the nanocomposites can exhibit an ultra-high dielectric constant, more than 1500 with a loss of about 1.0 at 1[Formula: see text]kHz, when the Ni content (53 vol.%) is close to percolation threshold. For the nanocomposites with 50 vol.% Ni particles, a dielectric constant more than 600 with a loss less than 0.2 is achieved. It is concluded that the loss including high loss is dominated by polarization process rather than the electrical conductivity. It is also found that the appearance of Ni particles has a strong influence on the crystallization process in the polymer matrix so that the polymer is converted from a typical ferroelectric to a relaxor ferroelectric. It is also demonstrated that the widely used relationship between the dielectric constant and the composition of the composites may not be valid.