Abstract:The Young's modulus and fracture toughness of sintered ceramic composites of the SiC-AlN system, which has a limited composition range of solid solution, were evaluated by a micromechanical analysis based on a microstructural modeling which took into account the microstructural features and solid solutioning.The Young's modulus of the composite, which depends on the volume fraction of dispersoids, Young's moduli and Poisson's ratios of the matrix and the dispersoids, was evaluated by Eshelby's method; a micromechanical approach to solve three-dimensional elasticity problems in which spherical dispersoids are embedded in a infinite elastic matrix. The fracture toughness of the composite was estimated by the Evans' formula which considered the thermal residual stress introduced during cooling from a sintering temperature, due to the difference in coefficient of thermal expansion (CTE) between the matrix and dispersoids. The thermal residual stresses of both for the dispersoids and the matrix were analyzed by Eshelby's method using the volume fraction of dispersoids, and Young's moduli and Poisson's ratios of the matrix and dispersoids. It was predicted that the thermal residual stress around dispersoids, which was introduced during processing, remarkably enhance the fracture toughness. Both of the predicted Young's modulus and the fracture toughness of the composite, particularly in the SiC-rich composition range, were in good agreement with the experimental values.

Young Modulus and Fracture-Toughness of Sic-Ain Composite