Coexistence of long-range ferromagnetic ordering and spin-glass behavior observed in the first inorganic–organic hybrid 1-D oxalate-bridging nona-MnII sandwiched tungstoantimonate chain

Jiancai Liu,Jie Luo,Qing Han,Jing Cao,Lijuan Chen,You Song,Junwei Zhao

DOI: https://doi.org/10.1039/c6tc05479j

IF: 6.4

2017-01-01

Journal of Materials Chemistry C

Abstract:A neoteric 1-D sinusoidal tungstoantimonate (TA) Na2H4{[Mn(H2O)(3)](3)[Mn(H2O)(2)](2)[Mn(H2O)][Mn(C2O4)](3)[B-alpha-SbW9O33](2)}center dot 31H(2)O (1) was synthesized from the reaction of Na-9[B-alpha-SbW9O33]center dot 19.5H(2)O with MnCl2 center dot 4H(2)O with the assistance of oxalic acid and structurally characterized by elemental analysis, IR spectroscopy, single-crystal X-ray diffraction, powder X-ray diffraction and thermal analyses. In 1, an unprecedented oxalate-bridging nona-MnII {[Mn(H2O)(3)](3)[Mn(H2O)(2)](2)[Mn(H2O)][Mn(C2O4)](3)}(12+) cluster is clamped by two trivacant Keggin [B-alpha-SbW9O33](9-) fragments forming a unique nona-Mn-II-encapsulated sandwich-type species. In the sandwich belt, the internal hexa-Mn-II {[Mn(H2O)(2)](2)[Mn(H2O)][Mn(C2O4)](3)}(6+) ring is alternately concatenated with three [Mn(H2O)(3)](2+) ions situated at three vertices of an equicrural triangle through oxalate linkers, completing an approximately coplanar nona-Mn-II core. More interestingly, adjacent nona-Mn-II-sandwiched TA units are interconnected by double Mn-II-C2O4 linkages, giving rise to the first inorganic-organic hybrid 1-D chain high-nuclear Mn-sandwiched TA. Furthermore, the zero-field-cooling/field-cooled magnetization and alternating current magnetic susceptibility measurements reveal the occurrence of long-range ferromagnetic ordering and spin-glass behavior in 1, which are further consolidated by the fitting of the Arrhenius law and the conventional critical scaling law of spin dynamics.