Abstract:Size-tunable beta-NaYF4: Yb/Er (50-400 nm) up-converting nanoparticles (UCNPs) with a strong green emission were successfully prepared by a facile thermal decomposition method in a short period of time. The effects of the reaction time, the oleic acid (OA) content, and the doped Gd3+ concentration on the crystal structure, the size evolution mechanism and the luminescence mechanism of the beta-NaYF4: Yb/Er nanoparticles were discussed in detail. Characterization was completed using X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution (HR-TEM), scanning electron microscopy (SEM), and photoluminescence (PL). The results reveal that the phase transition was completed at 15 min and the morphology of the NaYF4: Yb/Er UCNPs changed from spherical to large hexagonal disks (200-400 nm) in non-doped Gd3+. An appropriate decrease in the volume ratio of oleic acid (OA) to 1-octadecene (ODE) promoted NaF production, resulting in the formation of the hexagonal phase crystals and the subsequent increase of luminous intensity by 30-40 times. More importantly, the size of the beta-NaYF4: Yb/Er decreased with Gd3+ doping, and the UCNPs ultimately transformed into small hexagonal prisms (50 nm) with high monodispersity when the doping concentration of Gd3+ was 60 mmoL. The PL spectra confirmed that the luminous intensity of the UCNPs with doped Gd3+ was much higher than that of the undoped UCNPs. The results show that this route for UCNP fabrication with high luminous efficiency and a small size could be extended to other UCNP systems for multifunctional biomedical applications.

Enhanced Upconversion Fluorescence and Altered Particle Size of Β-Nagdf_4:Yb^3+/er^3+ Nanocrystals by Codoping with Mo^3+ Ions

Enhanced Upconversion Emission in Yb3+ and Er3+ Codoped NaGdF4 Nanocrystals by Introducing Li+ Ions.

Influence of Cr 3+ ions doping on growth and upconversion luminescence properties of β-NaYF 4 :Yb 3+ /Er 3+ microcrystals

Shape controllable synthesis and enhanced upconversion photoluminescence of ${{\beta }}$-NaGdF4:Yb3+, Er3+ nanocrystals by introducing Mg2+

Tin-(IV) dopant-controlled synthesis of Yb3+/Er3+:NaGdF4 nanocrystals: Morphology transformation and intensified upconversion performance

Enhancement and regulation of fluorescence emission from NaYF4:Yb3+, Er3+ nanocrystals by codoping Mn2+ ions.

Decrease in Particle Size and Enhancement of Upconversion Emission Through Y3+ Ions Doping in Hexagonal Naluf4:Yb3+/Er3+ Nanocrystals

Upconversion Luminescence and Energy‐Transfer Mechanism of NaGd(MoO4)2: Yb3+/Er3+ Microcrystals

Effect of Cr3+ and Alkaline-Earth Metal Ions Co-Doping on the Enhancement of Upconversion Luminescence in Β-Nayf4:Yb3+/er3+ Microparticles

The Upconversion Luminescence of Er3+/Yb3+/Nd3+ Triply-Doped β-NaYF₄ Nanocrystals under 808-nm Excitation.

Growth and Enhanced Upconversion Luminescence Intensity of Mg2+ and Cr3+ Co-Doped Β-Nayf4:Yb3+/er3+ Microcrystals

Size-tunable Β-Nayf4:Yb/er Up-Converting Nanoparticles with a Strong Green Emission Synthesized by Thermal Decomposition

Enhanced upconversion emission and magnetization in Yb3+-Er3+/Ho3+ codoped Gd2O3 nanocrystals by introducing Zn2+ ions

Enhanced up-conversion luminescence from NaYF4:Yb,Er nanocrystals by Gd3+ ions induced phase transformation and plasmonic Au nanosphere arrays

Enhanced Red Upconversion Luminescence By Codoping Ce3+ In Beta-Nay(Gd-0.4)F-4:Yb3+/Ho3+ Nanocrystals

Upconversion Improvement in KLaF4:Yb3+/Er3+ Nanoparticles by Doping Al3+ Ions

Enhancement of Upconversion Luminescence of Y2O3:Er3+ Nanocrystals by Codoping Li+–Zn2+

Influence of Na+ Ion Doping on the Phase Change and Upconversion Emissions of the GdF3: Yb3+, Tm3+ Nanocrystals Obtained from the Designed Molecular Precursors

Upconversion Luminescence Properties of Er3+ Doped Yb2ti2o7 Nanophosphor by Gd3+ Codoping

Comparative Investigation on Nanocrystal Structure and Luminescence Properties of Gadolinium Molybdates Codoped with Er 3+ /Yb 3+

Enhancement of Upconversion Emissions of NaYF4: Yb3+, Tm3+ Nanoparticles by Ba2+ Co-Doping