Preparation of WO3 based flexible electrochromic fabric and near infrared shielding application
Mengjie Li,Wei Jiang,Yun Lin,Chengjie Huang,Panpan Hao,Wenwen Wang,Liyan Yang,Yuedan Wang,Dong Wang
DOI: https://doi.org/10.1039/d4tc00403e
IF: 6.4
2024-03-12
Journal of Materials Chemistry C
Abstract:In this work, tungsten trioxide (WO3) film was prepared on carbon cloth using one-step hydrothermal method. All results revealed that a variety of WO3 nanostructures including nanoparticles, nanoplates, 3D nanorod flowers, nanorods, and nanobundle could be obtained by modulating pH of the precursor solution. The electrochromic performance of different nanostructure films has been investigated. The hexagonal WO3-1.6 present the highest electrochromic properties with a reflection contrast ΔR at 410 nm is 38.83%, a coloring and bleaching time of 2.59 and 5.29 s at 800 nm, respectively. The electrochromic fabric can realize the color change from light blue to blue purple to blue black in the voltage range of -1.2 V~1.5 V. There is no significant degradation of the electrochromic properties after 100 coloring/bleaching cycles, making it attractive for practical applications. In addition, electrochromic fabric in the field of near infrared thermal shielding was studied. When used as a window shielding, the difference of temperature rise (6.2 °C) in the container of WO3-1.6 colored state after light is significantly lower than that of carbon cloth (11.3 °C) or cotton cloth (11.8 °C). In the case of contact shielding, the temperature difference of the cotton cloth shielded by bleached sample before and after the same light is up to 2.6 °C. These results confirm that WO3 electrochromic fabric has good electrochromic and thermal shielding properties, and provide the possibility for the wearable functional applications of flexible electrochromic fabric.
materials science, multidisciplinary,physics, applied