Interfacial Morphologies and Erosion–corrosion Behavior of Directional Fe-3.5 Wt.% B Steel in Flowing Liquid Zn Containing 0.30 Wt.% Al

Yong Wang,Jiandong Xing,Shengqiang Ma,Baochao Zheng,Hanguang Fu,Guangzhu Liu

DOI: https://doi.org/10.1016/j.corsci.2016.07.007

IF: 7.72

2016-01-01

Corrosion Science

Abstract:The interfacial morphologies and erosion-corrosion behavior of directional Fe-3.5 wt.% B steel in flowing liquid Zn-0.30 wt.% Al were investigated. Adding 0.30 wt.% Al to liquid zinc significantly improved the erosion-corrosion resistance of directional Fe-3.5 wt.% B steel, which possesses greater erosion-corrosion resistance when the [002] orientation of Fe2B is perpendicular to the erosion-corrosion interface. The erosion-corrosion interface consisted of an inhibition layer, determined by 0.30 wt.% Al, liquid zinc temperature and Fe2B orientation. This interface inhibited the diffusion, controlled Fe2B failure mode, resisted micromechanical scouring, and suppressed erosion-corrosion. Deterioration of the inhibition layer at the erosion-corrosion interface resulted in severe erosion-corrosion damage. (C) 2016 Elsevier Ltd. All rights reserved.