Unveiling the Promotion Effects of CoO on Low-Temperature NO Reduction with CO over an In-Situ -Established Co 3 O 4 –CoO Heterostructure
Xinyang Wang,Ling Zhao,Xinyong Li,Jincheng Mu,Liehao Wei,Shiying Fan,Zhifan Yin,Liang Wang,Moses O. Tadé,Shaomin Liu,Moses O. Tadé
DOI: https://doi.org/10.1021/acssuschemeng.1c01593
2021-04-21
Abstract:Co-based catalysts have been widely applied in NO reduction by CO but still suffer from the unsatisfactory low-temperature catalytic performance. Here, a series of catalysts with a Co<sub>3</sub>O<sub>4</sub>–CoO heterointerface were <i>in-situ</i>-prepared and first applied into NO reduction by CO. Compared with single-phase samples, the catalysts with the Co<sub>3</sub>O<sub>4</sub>–CoO heterointerface exhibited superior catalytic performance. The best CoO<i><sub><i>x</i></sub></i>-350-7 sample showed a lowest apparent active energy (54.2 kJ·mol<sup>–1</sup>) and achieved 100% NO conversion at 150 °C (gas hourly space velocity = 50 000 h<sup>–1</sup>). The role of CoO as well as the structure–activity relationship between the interfacial effect and catalytic activity were deeply investigated. Abundant oxygen vacancies were induced due to the introduction of CoO species, and thus, the reducibility and oxygen migration of Co<sub>3</sub>O<sub>4</sub>–CoO catalysts were enhanced. The introduction of CoO not only optimized the NO adsorption but also enhanced electron donation ability from the catalyst to adsorbed NO. Moreover, the presence of CoO coupled with oxygen vacancies regulated the CO adsorption/conversion on the catalysts and thus promoted the exposure and reactivation of active sites for the reaction cycles. Accordingly, the stimulated dissociation of NO and the formation of −NCO could enhance the NO conversion to N<sub>2</sub> at lower and higher temperatures, respectively.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c01593?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c01593</a>.Thermal analysis profiles; XRD pattern of CoO<i><sub><i>x</i></sub></i> precursor and CoO<i><sub><i>x</i></sub></i>-<i>T</i>-3 samples; FT-IR spectra, N<sub>2</sub> adsorption–desorption isotherms, BJH pore size distribution curves, texture properties, XPS survey spectra and low-temperature EPR spectra, CO-TPD curves of Co<sub>3</sub>O<sub>4</sub>, CoO<i><sub><i>x</i></sub></i>-350-<i>t</i>, and CoO samples; N<sub>2</sub> yield of Co<sub>3</sub>O<sub>4</sub>, CoO<i><sub><i>x</i></sub></i>-350-<i>t</i>, and CoO samples; NO conversion of CoO<i><sub><i>x</i></sub></i>-450-<i>t</i> catalysts; catalytic stability test of CoO<i><sub><i>x</i></sub></i>-350-7 sample; NO conversion under different NO/CO ratios in reaction gas over CoO<i><sub><i>x</i></sub></i>-350-7; normalized reaction rates and Arrhenius plots for the rate of NO conversion over Co<sub>3</sub>O<sub>4</sub>, CoO<i><sub><i>x</i></sub></i>-350-<i>t</i>, and CoO catalysts; <i>in situ</i> DRIFTS spectra for CO adsorption for Co<sub>3</sub>O<sub>4</sub>, CoO<i><sub><i>x</i></sub></i>-350-7, and CoO catalysts; <i>in situ</i> DRIFTS spectra for NO adsorption and CO + NO coadsorption over CoO catalysts; schematic structure models of Co<sub>3</sub>O<sub>4</sub> {001}, CoO {100}, and Co<sub>3</sub>O<sub>4</sub>–CoO heterostructure; PDOS plots of Co<sub>3</sub>O<sub>4</sub> and CoO layers; adsorption energy of NO and Bader charge of NO; PDOS plots of NO on different Co<sub>3</sub>O<sub>4</sub> and CoO layers (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c01593/suppl_file/sc1c01593_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology