Highly Shape-Selective Synthesis of Monodispersed Fivefold Twinned Platinum Nanodecahedrons and Nano ACHTUNGRE icosahedrons
Wei Zhu,An-Xiang Yin,Ya-Wen Zhang,Chun-Hua Yan
2012-01-01
Abstract:Shape controllable synthesis of colloidal inorganic nanocrystals (e.g., noble metals, II–VI and III–V group semiconductors, metal oxides) has drawn continually increasing interest because of their unique shape-dependent material properties and the perspective new applications. Wellshaped noble-metal nanocrystals are of scientific and technological significance in multidisciplinary fields of catalysis, optics, magnetics, electronics, plasmonics, photonics, biology and medicine, etc. f, g] So far, various solution syntheses have been demonstrated as the robust approaches for manipulating the shape of single-crystalline and multiply twinned noble-metal nanocrystals (e.g., 1D wires and rods, 2D plates, regular and/or concave 3D polyhedrons and cubes with low or high Miller index facets) by virtue of their advantages both in finely tuning the reduction kinetics of the metal precursors and in readily controlling the subsequent nanocrystal growth regimes. Amongst them, the uses of facet-selective chemical agents (e.g., coordinative molecules and foreign ions) and facet-predefined seeds, together with the mediated reducing rates of metal precursors are key factors for precisely defining the nanocrystal shapes. Platinum-based catalysts are noteworthy for their wide uses in oil refinement, fine chemicals, and fuel cells, etc. Recently, much attention has been paid to shape controlled synthesis and catalytic reactivities of monodispersed Pt nanoparticles (NPs), which provide well-defined models for comprehending the relevance between morphology and catalytic properties (activity, selectivity and durability), for bridging the material gap between single crystal and industrial catalysis. So far, well-shaped Pt NPs with exposed basal facets, such as {111}, {100} and {110} (e.g., tetrahedron, octahedron, cube, cubo-octahedron) d,e, g] and high index facets, such as {730} and {411} (e.g., tetrahexahedrons and concave nanocrystals) f, h] have been prepared by some solution methods, most of these NPs are single-crystalline. However, highly-strained Pt multiply twinned particles (MTPs) have been rarely synthesized; 6] the selective synthesis of Pt decahedrons and icosahedrons in fivefold twinned structures thus remains a challenging issue. Herein, we demonstrate a general and facile solid–liquid interface mediated reduction route towards highly shape-selective synthesis of monodispersed Pt nanodecahedrons (NDs) and nanoACHTUNGTRENNUNGicosahedrons (NIs). By the reduction of linear Pt complexes of Magnus green salt (MGS, [Pt ACHTUNGTRENNUNG(NH3)4]ACHTUNGTRENNUNG[PtCl4]) and methylamine substituted Magnus green salt (MSMGS, [Pt ACHTUNGTRENNUNG(CH3NH2)4]ACHTUNGTRENNUNG[PtCl4]) (for characterization details see Figures S1–S3 in the Supporting Information) with strong metal–metal interactions in oleylamine (OAm), respectively, monodispersed Pt NDs and NIs were synthesized with high shape selectivities. As illustrated in transmission electron microscope (TEM) and high resolution transmission electron microscope (HRTEM) images (Figure 1 and Figure S4 in the Supporting Information) the Pt NDs obtained with a size of 17.0ACHTUNGTRENNUNG( 1.5) nm (333 particles were counted) and selectivity of 70 % (after centrifugal separation, 877 particles were counted) were bounded with ten (111) facets. The Pt NIs with a size of 12.6 ACHTUNGTRENNUNG( 0.8) nm (318 particles were counted) and selectivity of 88 % (after centrifugal separation, 1244 particles were counted) were bounded with twenty (111) facets. The distinctly observed twin boundaries and fast Fourier transform (FFT; Figure 1 b, d, e, f) results confirmed that both of the structures were multiply twinned crystalline NPs. By comparing two-, three-, and fivefold symmetry HRTEM lattice fringes of the quasi-sphere Pt NPs (Figure 1 d, e, f) with previous HRTEM simulations of gold NIs with similar sizes, it was deduced that the geometry of these Pt NPs should have an icosahedral structure. Furthermore, high angle annular dark field-scanning transmission electron microscopy (HAADF-STEM; Figure S5 in the Supporting Information) affirmed the morphologies of Pt NDs and NIs. The contrast of HAADF-STEM images illustrated that the center of both Pt NDs and NIs was thicker than its edge. The contrast and profile of these Pt NPs fit well with the forecasted structures. Powder X-ray Diffraction (PXRD) results verified the purity and fcc structure of the Pt MTPs, and the broadened peaks confirmed the small sizes (Figure S6 in the Supporting Information). The reactions were conducted in glass-made colorimetric cylinders (10 mL) with stoppers. Several milligrams of precursor (solid) and OAm (10 mL, liquid) were mixed in cylinders, and the products were formed at either 130 or 150 8C [a] W. Zhu, A.-X. Yin, Prof. Dr. Y.-W. Zhang, Prof. Dr. C.-H. Yan Beijing National Laboratory for Molecular Sciences State Key Laboratory of Rare Earth Materials Chemistry and Applications, College of Chemistry and Molecular Engineering Peking University, Beijing, 100871 (P.R. China) Fax: (+86) 10-6275-6787 E-mail : ywzhang@pku.edu.cn yan@pku.edu.cn Supporting information for this article is available on the WWW under http://dx.doi.org/10.1002/chem.201201099.