Abstract:In this work, the structural and magnetic transitions of Heusler alloy Ni50Mn34In14Ga2 have been carefully studied through measurements of heat flow and magnetization under DC and AC magnetic fields. This alloy undergoes the transition sequence of spin-glassy martensite (SPM) → ferromagnetic austenite (FA) → paramagnetic austenite at ∼225 and ∼305 K, respectively, during heating. Splitting of zero-field-cooling (ZFC)/field-cooling (FC) curves in martensite is caused by the slowdown dynamics of spin glass as evidenced by frequency dispersion and aging effects. The development of a spin-glass state is believed to be the result of strain relaxation and interaction of ferroelastic twin walls in the martensite. The magnetocaloric effect (MCE) at the SPM–FA transition was then measured using indirect, quasi-direct, and direct methods. The MCE magnitudes are controlled by the entropy changes associated with the first-order martensite transition and magnetic ordering of austenite under the magnetic field. The existence of a spin-glass state in martensite can also improve the reversibility of the magnetostructural transitions, which is beneficial for the improvement of the reversibility of associated MCE. These results provide an in-depth understanding of the transitions and magnetic properties of the Ni–Mn Heusler alloys and suggest that the MCE at the first-order magnetostructural transitions estimated solely using indirect methods may need some revision.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c11308?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c11308</a>.SEM morphology image, EDX elemental mapping, EDX spectrum of the Ni50Mn34In14Ga2 alloy; χ′–T curves of NiMnInGa2; and Vogel–Fulcher fitting results (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11308/suppl_file/am0c11308_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Large spontaneous exchange bias and giant magnetoresistance in Ni50Mn37−xFexIn13(x=2–4) Heusler alloys

Large Field-Induced Magnetocaloric Effect in Ni$_{43}$Mn$_{46 - {\rm X}}$v$_{\rm X}$sn$_{11}$ Heusler Alloys

Enhanced Antiferromagnetic Interaction-Induced Spontaneous Exchange Bias in Mn 50 Ni 40 Sn 10-X Ti X Heusler Alloys

Magnetism And Magnetoresistance Studies Of Hffe6ge6-Type Y1-Xcexmn6sn6 (X=0.1-0.3) Compounds

Effect of Fe doping on the phase transitions,magnetocaloric effect and exchange bias in Mn50 Ni41-x Fex Sn9 alloys

A Giant Exchange Bias Effect Due to Enhanced Ferromagnetism Using a Mixed Martensitic Phase in Ni50Mn37Ga13 Spun Ribbons

Superposition of Conventional and Spontaneous Exchange Bias in a Ni50Mn34In13Fe3 Magnetic Shape Memory Alloy

Large magnetocaloric effect and exchange bias properties in Mn-Ni-Co-Sn full Heusler alloy

Giant Exchange Bias Effect In All-3d-Metal Ni38.8co2.9mn37.9ti20.4 Thin Film

Large Exchange Bias Field in the Ni–Mn–Sn Heusler Alloys with High Content of Mn

Magnetic-field-induced Reverse Martensitic Transformation and Large Magnetoresistance in Ni50−xCoxMn32Al18 Heusler Alloys

Large Magnetocaloric Effect and Magnetoresistance in Fe and Co Co‐Doped Ni‐Mn‐Al Heusler Alloys

Large Exchange Bias Triggered by Transition Zone of Spin Glass

Magnetic Phase Separation And Exchange Bias In Off-Stoichiometric Ni-Mn-Ga Alloys

Superspin glass behavior and giant exchange bias effect in hexagonal (Mn0.7Cu0.3)66Ga34 ferrimagnet

Tuning Antiferromagnetic Exchange Interaction for Spontaneous Exchange Bias in MnNiSnSi System

Large Magnetoresistance and Magnetic Field Induced Strain in Ni42.8Co7.7Mn38.8Al10.7 Heusler Alloy at Room Temperature

Microstructure, first-order magnetostructural transition, magnetocaloric properties and exchange bias effect in Ni45−xBixMn44Sn11 alloys

Glassy Magnetic Transitions and Accurate Estimation of Magnetocaloric Effect in Ni–Mn Heusler Alloys

Spin Cluster Size Dependence of Exchange Bias Effect in Mn50Ni40Ga10 Heusler Alloys

Magnetic-Field-Induced Strains And Magnetic Properties Of Heusler Alloy Ni52mn23ga25