Abstract:Organometal trihalide perovskites are emerging as a new generation of photovoltaic materials. They are abundant in nature and have rapidly increasing power conversion efficiencies (PCE) of above 15% in common hybrid (mixed organic/inorganic) thin-film-based solar cells.1–3 Up to now, perovskite films have been formed by film deposition approaches such as spin-coating, sequential deposition of the inorganic and organic precursor, and co-evaporation of the precursors.1, 2 Low-temperature solution processes are among the simplest ways to fabricate planar low-cost photovoltaic devices. However, perovskite crystallizes very rapidly, so it is very challenging to form uniform, continuous, and leakage-free perovskite films by solution methods.2 We developed two simple and effective low-temperature solution processes to fabricate high-efficiency perovskite devices (see Figure 1). In the first approach, we studied the influence of the ratio of the precursors methylammonium iodide (CH3NH3I) and lead iodide (PbI2) in a premixed solution. 3 We found that using a non-stoichiometric precursor solution (i.e., not in a simple ratio) was critical to forming stoichiometric (i.e., in a simple ratio) perovskite films. The compositions of the spun perovskite films were very sensitive to the substrate surface, and could be very different from those of the precursor solutions. We varied the composition of the precursor solution, and found a PbI2/CH3NH3Xmolar ratio of 0.6–0.7 gave the best surfacemorphology and electronic properties, such as doping concentration. We used a planar heterojunction device structure of ITO/ PEDOT:PSS/(CH3NH3I)/PCBMor ICBA/C60/BCP/aluminum, where ITO is a substrate of indium tin oxide, PEDOT:PSS is an electron-donating transparent conductive polymer, PCBM and ICBA are fullerene-derived electron acceptors, C60 is buckminsterfullerene (a spherical fullerene molecule), and BCP is 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline, an electrontransporting but hole-blocking layer. Figure 1. Schematic of the prepation of perovskite films by (a) spin coating of pre-mixed precursor of lead iodide (PbI2) and methylammonium iodide (CH3NH3I) and (b) an interdiffusion approach. ITO: Indium tin oxide, a transparent conducting oxide. PEDOT:PSS: A transparent, conductive polymer. MAI: Methylammonium iodide. MAPbI3 Methylammonium lead iodide.

Large-area, high-quality organic–inorganic hybrid perovskite thin films via a controlled vapor–solid reaction

Vapor-assisted solution process for perovskite materials and solar cells

Enhancing Organic‐Inorganic Perovskite Thin Film Crystallization via Vapor‐Solid Reaction by Modifying PbI2 Precursors films with Pyridinium Trifluoromethanesulfonate

Improving the Crystal Growth of a Cs0.24FA0.76PbI3−xBrx Perovskite in a Vapor–solid Reaction Process Using Strontium Iodide

Combined Vacuum Evaporation and Solution Process for High‐Efficiency Large‐Area Perovskite Solar Cells with Exceptional Reproducibility

Crystalline Quality Control In Sequential Vapor Deposited Perovskite Film Toward High Efficiency And Large Scale Solar Cells

Uniform, High Crystalline, (100) Crystal Orientated Perovskite Films Without PbI2 Residue by Controlling the Nanostructure of PbI2

Precise phase control of large-scale inorganic perovskites via vapor-phase anion-exchange strategy

Precise Phase Control of Large‐Scale Inorganic Perovskites via Vapor‐Phase Anion‐Exchange Strategy

Organic solvent vapor sensitive methylammonium lead trihalide film formation for efficient hybrid perovskite solar cells

Oriented Growth for Efficient and Scalable Perovskite Solar Cells by Vapor–Solid Reaction

Preparing High-Efficiency Perovskite Solar Cells

Preperation of Perovskite Materials and Perovskite Solar Cells by Vapor-Assisted Solution Process

A stress relaxation strategy for preparing high-quality organic-inorganic perovskite thin films via vapor-solid reaction

Large Area Perovskite Solar Cell Via Two-step Ultrasonic Spray Deposition

Vapor-Assisted Crystallization Control Toward High Performance Perovskite Photovoltaics With Over 18% Efficiency In The Ambient Atmosphere

Fast and Controllable Electric-Field-Assisted Reactive Deposited Stable and Annealing-Free Perovskite toward Applicable High-Performance Solar Cells

Facile preparation of organometallic perovskite films and high-efficiency solar cells using solid-state chemistry

Key parameters of two typical intercalation reactions to prepare hybrid inorganic–organic perovskite films

Planar Heterojunction Perovskite Solar Cells Via Vapor-Assisted Solution Process

Effects of Lead Iodide Crystallization on Photovoltaic Performance of Perovskite Solar Cells by the Vapor-Solid Reaction Method