Synthesis of WO_3−x Nanomaterials with Controlled Morphology and Composition for Highly Efficient Photocatalysis

Beijing University of Posts and Telecommunications,Zhao Zengying,Peng Zhijian,Fu Xiuli

DOI: https://doi.org/10.1557/jmr.2016.106

2016-01-01

Abstract:Tungsten oxide (WO_3−x) nanomaterials with controlled morphology and composition were fabricated by thermal evaporation of WO_3 and S powders at different temperatures in a vacuum tube furnace. At 850 °C the obtained green particle is still of the same monoclinic WO_3 phase as that of the starting powder. At a temperature between 900 and 1100 °C, the resultant dark-blue products are particle-like clusters composed of numerous monoclinic WO_2.90 short nanorods, but the clusters became looser and the nanorods grew somewhat longer as the temperature increased. At a temperature between 1150 and 1250 °C, elongated and thoroughly separate purple-red monoclinic W_18O_49 nanorods were obtained. The growth of the prepared WO_3−x nanomaterials was controlled by a gas–solid mechanism. Their photocatalytic degradation on organic contaminants was evaluated by decomposing methylene blue (MB) in aqueous phase under sunlight, in which WO_3 particles presented higher photocatalytic activity than its oxygen-deficient counterparts, WO_2.90 and W_18O_49. But the W_18O_49 nanorods had higher adsorption ability to MB in all the samples.