Synthesis of Α-Fe2o3/bi2wo6 Layered Heterojunctions by in Situ Growth Strategy with Enhanced Visible-Light Photocatalytic Activity

Taiping Xie,Yue Liu,Haiqiang Wang,Zhongbiao Wu

DOI: https://doi.org/10.1038/s41598-019-43917-w

IF: 4.6

2019-01-01

Scientific Reports

Abstract:Layered heterojunction structure with larger interface region for electron migration has attracted much attention in recent years. In this work, layered α-Fe2O3/Bi2WO6 heterojunctions with strong interlayer interaction were successfully synthesized through a facile in situ growth method. The strong interaction between α-Fe2O3 and Bi2WO6 had resulted in excellent photoelectrochemical performance. It was found that such structure promoted the interfacial photogenerated charges separation according to EIS and Tafel analysis, except for the expansion of visible-light absorption range. PL and TRPL characterizations further demonstrated that the recombination ratio of photoexcited electron-hole pairs was greatly reduced. The toluene photocatalytic degradation tests had showed that α-Fe2O3/Bi2WO6 composites exhibited much well activity under visible-light irradiation. Especially, 4%-Fe2O3/Bi2WO6 sample displayed the highest photocatalytic activity, which was around 3 and 4 times higher than that of pure Bi2WO6 and α-Fe2O3. Based on ESR results and free radical trapping experiments, hydroxyl radicals (·OH) and holes (h+) were regarded as the main active species. The establishment of Fe2O3/Bi2WO6 with layered heterojunctions could provide new insights into the construction of novel photocatalysts.