Adaptability analysis of H 2 -rich gas injection and sintered ore performance with different raw material ratios
Yaqiang Yuan,Tao Rong,Yuanhao Yu,Huafang Yu,Hao Guo,Yan Gao,Jingsong Wang,Qingguo Xue,Haibin Zuo
DOI: https://doi.org/10.1016/j.jmrt.2024.10.169
IF: 6.267
2024-10-21
Journal of Materials Research and Technology
Abstract:As a source substitution technology that reduces pollutants emission and optimizes sinter properties, H 2 -rich gas injection-assisted iron ore sintering holds significant practical value. This study analyzed the adaptability of this technology to different ore blend ratios and basicity levels by comparing sintering indexes, pore structure, mineral phase composition, and metallurgical performance before and after H 2 -rich gas injection. The carbon emission reduction following H 2 -rich gas injection was calculated. The results indicate that increasing the proportion of high-silica, low-alumina ore (Ore-A) and basicity, along with H 2 -rich gas injection, can effectively enhance sinter yield and quality, but shrink the pore structure of sinter. Under H 2 -rich gas injection conditions, decreasing Ore-A ratios and increasing basicity can augment SFCA phase formation and mineral phase uniformity, thereby improving the anti-pulverization ability and reductivity of the sinter. H 2 -rich gas injection presents better adaptability to sintered ore with lower Ore-A ratio and basicity, which can achieve greater improvements in the sintering indexes, RDI, and RI. For a 265 m 2 sinter plant producing sinter with 18 wt% Ore-A and 2.0 basicity, annual CO 2 emissions can be reduced by approximately 40,000 t.
materials science, multidisciplinary,metallurgy & metallurgical engineering