Binary NiCu Layered Double Hydroxide Nanosheets for Enhanced Energy Storage Performance As Supercapacitor Electrode

Teng Wang,Shengli Zhang,Hongxia Wang

DOI: https://doi.org/10.1007/s40843-017-9131-7

2017-01-01

Science China Materials

Abstract:Owing to the high power density and long-term stability characteristics, supercapacitors (SCs), also called electrochemical capacitors, have attracted great interests as one of the most efficient electrical energy storage devices [1]. According to the charge storage mechanism of the electrode, SCs are classified into electric double layer capacitors (EDLC) which store charges via static electrolyte ion adsorption/desorption, and pseudo-capacitors (PSC) which involve a faradaic redox reaction process. PSCs have attracted lots of attention recently because of their advantage of higher energy storage ability than EDLC to meet broader applications [2]. The energy density of a PSC strongly depends on the nature of the electrode material and the material morphology. Candidate materials including transition metal oxides/ hydroxides/chalcogenides/phosphides, conductive polymers, and MXene materials have been reported to possess good pseudocapacitive properties [3–9]. Specially, PSCs based on nickel hydroxide/layered double hydroxide (LDH) have been investigated extensively due to their high theoretical capacitance [10–12]. Nevertheless, experimentally the electrochemical properties of NiLDH such as specific capacitance and rate capability are normally unsatisfactory due to the poor conductivity and fragile crystalline structure of the material. One approach to solve this problem is through introduction of additional metal ions such as cobalt and aluminium to make binary LDH [13–16]. As an earth-abundant element, Cu based hydroxide materials recently received limited interest in application in SCs [17–20]. For example, Pramanik et al. [20] reported a Cu(OH)2@RGO composite, which exhibited a specific capacitance of 602 F g at a small current density of 0.2 A g. However, the materials normally show an unsatisfied energy storage ability including a low specific capacitance and low conductivity. Zheng et al. [21] recently reported NiCu carbonate hydroxide nanowire arrays formed on Cu foam. The material exhibited a promising supercapacitive performance (971 F g at 1 A g). Nevertheless, the capacitance is still unsatisfactory which is even lower than single metal NiLDH materials [11]. Moreover, the rigidity of the Cu foam limits its application in wearable devices, which has recently been regarded as one of the main developing directions for advanced SCs [22–24]. Clearly more indepth research of NiCu LDH is needed to explore its potential as electrode material for SC application. Herein, we demonstrate a facile way to enhance the electrochemical properties of NiLDH nanosheet arrays which was directly grown on carbon fiber cloth (CFC) through incorporation of Cu via a one-step solvothermal method. The as-prepared NiCuLDH material demonstrated significantly increased specific capacitance (1953.5 F g at 0.5 A g), excellent rate stability and conductivity. The NiCuLDH material was synthesized using the modified solvothermal method we reported recently [13]. In this one-step reaction, 2-methylimidazole (MIM) and pure methanol were used as surfactant and solvent respectively. The NiCuLDH with precursor ratio of Ni/ Cu=1 (named NiCuLDH(10-10)) was firstly made and used for characterization. Fig. 1a reveals the field emission scanning electron microscope (FESEM) image of bare carbon fibers which show a smooth surface. After the solvothermal reaction, the carbon fiber is uniformly