Abstract:The intimate interplay of chitosan (CS) and graphene oxide (GO) in aqueous acidic solution has been explored to design upon casting, nanostructured "brick-and-mortar" films (CS-GO-f) and by acidic-to-basic pH inversion, porous CO2-dried aerogel microspheres (CS-GO-m). Owing to the presence of oxygenated functional groups in GO, good-quality crack-free hybrid films were obtained. Mechanical properties were improved independently of the GO content and it was found that a 20wt% loading affords hybrid film characterized with a Young modulus three times superior to that reached with the same loading of layered clay. The presence of graphene oxide was found to be detrimental for the thermal stability of the polysaccharide at T <350°C, a fact attributed to the well-established decomposition of the oxygenated functional groups of the graphene sheets. Irrespective to the graphene oxide loading, chitosan-graphene oxide mixture preserves the gelation memory of the polysaccharide. Supercritical drying of the resulting soft hydrogels provides macroporous network with surface areas ranging from 226m2g-1 to 554m2g-1. XPS and RAMAN analyses evidenced the selective reduction of GO sheets inside of these microspheres, affording the hitherto unknown macroporous chitosan-entangled-reduced graphene oxide (CS-rGO-m) aerogels. Improvement in both hydrothermal stability (under water reflux) and chemical stability (under acidic conditions) have been noticed for chitosan-graphene oxide microspheres with respect to non-modified chitosan and chitosan-clay bio-hybrids, a result rooted in the substantial hydrophobic character imparted by the addition of graphenic material to the polysaccharide skeleton. In essence, this contribution demonstrates that graphene oxide loading do not disturb neither the filmogenicity of chitosan nor its gelation ability and constitutes a promising route for novel chitosan-based functional hybrid materials.

60Co Γ-Ray Irradiation Crosslinking of Chitosan/Graphene Oxide Composite Film: Swelling, Thermal Stability, Mechanical, and Antibacterial Properties

Graphene Oxide/cellulose Composite Films with Enhanced UV-shielding and Mechanical Properties Prepared in NaOH/urea Aqueous Solution

Effect of graphene oxide content on the tensile properties and swelling ratio of chitosan/xanthan gum/graphene oxide hydrogel films

Graphene Oxide-Reinforced Biodegradable Genipin-Cross-Linked Chitosan Fluorescent Biocomposite Film and Its Cytocompatibility

Investigation on Baicalin‐loaded Chitosan Film Crosslinked by Graphene Oxide and Its Biocompatibility

Effect of 60Co irradiation on the properties of chitosan rod

Chitin/graphene Oxide Composite Films with Enhanced Mechanical Properties Prepared in NaOH/urea Aqueous Solution

Preparation and Characterization of Chitosan/poly(vinyl Alcohol)/graphene Oxide Films and Studies on Their Antibiofilm Formation Activity

Synthesis, Characterization, and Bactericidal Evaluation of Chitosan/Guanidine Functionalized Graphene Oxide Composites

Preparation and Properties of Cross-linked Gliadin/chitosan Films

In Situ Reduction of Graphene Oxide Nanosheets in Poly(vinyl Alcohol) Hydrogel by Γ-Ray Irradiation and Its Influence on Mechanical and Tribological Properties

Green fabrication, characterization and antimicrobial activities of AgO/Ag/carboxymethyl chitosan- graphene oxide films

Chitosan-graphene oxide films and CO2-dried porous aerogel microspheres: Interfacial interplay and stability

Development of chitosan, graphene oxide, and cerium oxide composite blended films: structural, physical, and functional properties

PREPARATION AND PROPERTIES OF CHITOSAN-GRAFT-POLY(ACRYLIC ACID)/GRAPHENE OXIDE NANOCOMPOSTIE HYDROGELS

Adjustable dielectric and bioactivity characteristics of chitosan-based composites via crosslinking approach and incorporation of graphene

Enhanced mechanical strength and antibacterial properties of Chitosan/Graphene oxide composite fibres

Synthesis and Characterization of Graphene Oxide/Chitosan Composite Aerogels with High Mechanical Performance

Graphene Oxide–polyoctahedral Silsesquioxane–chitosan Composite Films with Improved Mechanical and Water‐vapor‐transport Properties

Effect of Gamma Irradiation on the Condensed State Structure and Mechanical Properties of Konjac Glucomannan/chitosan Blend Films

The Fabrication of Cassava Silk Fibroin-Based Composite Film with Graphene Oxide and Chitosan Quaternary Ammonium Salt as a Biodegradable Membrane Material