Abstract:Background: With the ageing of the population and the increase of sports injuries, the number of joint injuries has increased greatly. Tissue engineering or tissue regeneration is an important method to repair articular cartilage defects. While it has recently been paid much attention to use bilayered porous scaffolds to repair both cartilage and subchondral bone, it is interesting to examine to what extent a bilayer scaffold composed of the same kind of the biodegradable polymer poly(lactide-co-glycolide) (PLGA) can restore an osteochondral defect. Herein, we fabricated bilayered PLGA scaffolds and used a rabbit model to examine the efficacy of implanting the porous scaffolds with or without bone marrow mesenchymal stem cells (BMSCs). The present manuscript reports the regenerative potential up to 24 weeks. Methods: The osteochondral defect, 4 mm in diameter and 5 mm in depth, was created in the medial condyle of each knee in 23 rabbits. The bilayered PLGA scaffolds with a pore size of 100 -200 mu m in the chondral layer and a pore size of 300-450 mu m in the osseous layer, seeded with or without BMSCs in the chondral layer, were then transplanted into the osteochondral defect of each knee. The osteochondral defect created in the same manner was untreated to act as the control. At 12 and 24 weeks postoperatively, condyles were harvested and analyzed using histology, immunohistochemistry, real-time polymerase chain reaction, and biomechanical testing to evaluate the efficacy of osteochondral repair. Results: No joint erosion, inflammation, swelling, or deformity was observed, and all animals maintained a full range of motion. Compared with the untreated blank group, the groups implanting the bilayered scaffolds with or without cells exhibited much better resurfacing, similar to the surrounding normal tissue. The histological scores of neotissues repaired by the scaffold with cells were closer to that of normal tissue. Although the biomechanical properties of neotissues were not as good as the normal tissue, no significant difference was found between the gene levels of neotissues repaired by the scaffold with or without cells and that of the normal tissue. The repair of the osteochondral defect tends to be stable 12 weeks after implantation. Conclusions: Our bilayered PLGA porous scaffold supports long-term osteochondral repair via in vivo tissue engineering or regeneration, and its effect can be further facilitated under the scaffold seeded with allogenic BMSCs. The translational potential of this article: The bilayered PLGA porous scaffold can facilitate the repair of osteochondral defects and has potential for application in osteochondral tissue engineering. (C) 2019 The Authors. Published by Elsevier (Singapore) Pte Ltd on behalf of Chinese Speaking Orthopaedic Society.

Bilayered PLGA/PLGA-HAp Composite Scaffold for Osteochondral Tissue Engineering and Tissue Regeneration.

Osteochondral repair using porous poly(lactide-co-glycolide)/nano-hydroxyapatite hybrid scaffolds with undifferentiated mesenchymal stem cells in a rat model.

Feasibility of constructing a scaffold for osteochondral tissue engineering using poly(lactide-co-glycolide) alone

3D Printing of Biomimetic Multi-Layered GelMA/nHA Scaffold for Osteochondral Defect Repair

Tissue-engineered Composite Scaffold of Poly(lactide-Co-glycolide) and Hydroxyapatite Nanoparticles Seeded with Autologous Mesenchymal Stem Cells for Bone Regeneration.

Biphasic CK2.1-coated Β-Glycerophosphate Chitosan/ll37-Modified Layered Double Hydroxide Chitosan Composite Scaffolds Enhance Coordinated Hyaline Cartilage and Subchondral Bone Regeneration

Osteogenesis and Chondrogenesis of Biomimetic Integrated Porous Pva/Gel/V-N-Ha/Pa6 Scaffolds and Bmscs Construct in Repair of Articular Osteochondral Defect

Restoration of Osteochondral Defects by Implanting Bilayered Poly(lactide-Co-glycolide) Porous Scaffolds in Rabbit Joints for 12 and 24 Weeks

Bi-Layered Composite Scaffold For Repair Of The Osteochondral Defects

Bilayered Scaffold Prepared from a Kartogenin-Loaded Hydrogel and BMP-2-Derived Peptide-Loaded Porous Nanofibrous Scaffold for Osteochondral Defect Repair

A biomimetic bi-layered tissue engineering scaffolds for osteochondral defects repair

Bioactive Stratified Polymer Ceramic-Hydrogel Scaffold for Integrative Osteochondral Repair

Rat Cartilage Repair Using Nanophase Plga/Ha Composite and Mesenchymal Stem Cells

Preparation and characterization of biomimetic gradient multi-layer cell-laden scaffolds for osteochondral integrated repair

A composite scaffold of MSC affinity peptide-modified demineralized bone matrix particles and chitosan hydrogel for cartilage regeneration

Integrated and Bifunctional Bilayer 3D Printing Scaffold for Osteochondral Defect Repair

Fabrication and Development of Artificial Osteochondral Constructs Based on Cancellous Bone/hydrogel Hybrid Scaffold

Construction of tissue engineered cartilage in vivo with poly(lactide-co-glycolic acid) composited with collagen II and growth factors

The Phenotype of Mesenchymal Stromal Cell and Articular Chondrocyte Cocultures on Highly Porous Bilayer Poly-L-Lactic Acid Scaffolds Produced by Thermally Induced Phase Separation and Supplemented with Hydroxyapatite

Bilayered HA/CS/PEGDA hydrogel with good biocompatibility and self-healing property for potential application in osteochondral defect repair

Construction of Tissue-Engineered Osteochondral Composite Using Poly-Lactide-co-glyco-lide and Piuronic-F127 As the Scaffold: A Study of Interracial Compatibility