Abstract:The recent report of pressure-induced structural transition and signature of superconductivity with T c ≈ 80 K above 14 GPa in La 3 Ni 2 O 7 crystals has garnered considerable attention. To further elaborate this discovery, we carried out comprehensive resistance measurements on La 3 Ni 2 O 7 crystals grown in an optical-image floating zone furnace under oxygen pressure (15 bar) using a diamond anvil cell (DAC) and cubic anvil cell (CAC), which employ a solid (KBr) and liquid (glycerol) pressure-transmitting medium, respectively. Sample 1 measured in the DAC exhibits a semiconducting-like behavior with large resistance at low pressures and gradually becomes metallic upon compression. At pressures P ⩾ 13.7 GPa we observed the appearance of a resistance drop of as much as ∼ 50% around 70 K, which evolves into a kink-like anomaly at pressures above 40 GPa and shifts to lower temperatures gradually with increasing magnetic field. These observations are consistent with the recent report mentioned above. On the other hand, sample 2 measured in the CAC retains metallic behavior in the investigated pressure range up to 15 GPa. The hump-like anomaly in resistance around ∼ 130 K at ambient pressure disappears at P ⩾ 2 GPa. In the pressure range of 11–15 GPa we observed the gradual development of a shoulder-like anomaly in resistance at low temperatures, which evolves into a pronounced drop of resistance of 98% below 62 K at 15 GPa, reaching a temperature-independent resistance of 20 μΩ below 20 K. Similarly, this resistance anomaly can be progressively shifted to lower temperatures by applying external magnetic fields, resembling a typical superconducting transition. Measurements on sample 3 in the CAC reproduce the resistance drop at pressures above 10 GPa and realize zero resistance below 10 K at 15 GPa even though an unusual semiconducting-like behavior is retained in the normal state. Based on these results, we constructed a dome-shaped superconducting phase diagram and discuss some issues regarding the sample-dependent behaviors on pressure-induced high-temperature superconductivity in the La 3 Ni 2 O 7 crystals.

High-pressure Phase Diagram of NdFeAsO0.9F0.1: Disappearance of Superconductivity on the Verge of Ferromagnetism from Nd Moments

PHYSICAL REVIEW B 98, 094504 (2018) High-pressure phase diagram of NdFeAsO0.9F0.1: Disappearance of superconductivity on the verge of ferromagnetism from Nd moments

Struture Stability and Compressibility of Iron-Based Superconductor Nd(O<sub>0.88</sub>F<sub>0.12</sub>)FeAs under High Pressure

Pressure-Induced Phase Coexistence in Bafe1.8co0.2as2

Pressure-induced Phase Transitions and Correlation Between Structure and Superconductivity in Iron-Based Superconductor Ce(O(0.84)F(0.16))FeAs.

Pressure-induced Superconducting State of Antiferromagneticcafe2as2

Pressure-Induced Superconductivity in Lafeaso: the Role of Anionic Height and Magnetic Ordering

Emergence of High-Temperature Superconducting Phase in Pressurized La3Ni2O7 Crystals

Pressure-induced isostructural phase transition and correlation of FeAs coordination with the superconducting properties of 111-Type Na 1-xFeAs

Expansion of the Tetragonal Magnetic Phase with Pressure in the Iron Arsenide Superconductor Ba1−xKxFe2As2

Hole doping by pressure on the 1111 pnictides CaFeAsF and SrFeAsF

Pressure Effects on the Electronic Properties of the Undoped Superconductor ThFeAsN

Specific Heat and Phase Diagrams of Single Crystal Iron Pnictide Superconductors

Hall effect and magnetoresistance in single crystals of NdFeAsO

High-Pressure Evolution Of The Specific Heat Of A Strongly Underdoped Ba(Fe0.963co0.037)As-2 Iron-Based Superconductor

Pressure induced Lifshitz transition and anomalous crystal field splitting in AFeAs (A=Li/Na) Fe-based superconducting compounds: A first principles study

Universal V-shaped Temperature-Pressure Phase Diagram in the Iron-Based Superconductorskfe2as2,rbfe2as2, And

Pressure-Induced Shift of T-C and Structural Transition in "122" Type Pnictide Superconductor Ca0.34na0.66fe2as2

Emergence of high-temperature superconducting phase in the pressurized La3Ni2O7 crystals

Correlation Between Superconductivity and Structural Properties under High Pressure of Iron Pnictide Superconductor Ce0.6y0.4feaso0.8f0.2

Simultaneous optimization of spin fluctuations and superconductivity under pressure in an iron-based superconductor