Large aspect ratio gold nanorods (LAR-GNRs) for mid-infrared pulse generation with a tunable wavelength near 3 μm.

Hongyu Luo,Zhe Kang,Ying Gao,Hanlin Peng,Jianfeng Li,Guanshi Qin,Yong Liu

DOI: https://doi.org/10.1364/OE.27.004886

IF: 3.8

2019-01-01

Optics Express

Abstract:We report a tunable passively Q-switched fiber laser at the wavelengths near 3 mu m. using large aspect ratio gold nanorods (LAR-GNRs) as a saturable absorber (SA) for the first time. The GNRs with a large average aspect ratio of up to similar to 20 were prepared using the seed-mediated growth method, which yielded a strong absorption band of 2.2-3 mu m with a peak at similar to 2600 nm, stemming from longitudinal surface plasmon resonance (SPR). The corresponding nonlinear absorption was characterized using 2.87 mu m ultrafast pulses, giving the modulation depth of 8.89%, saturation intensity of 14.9 MW/cm(2), and nonsaturation loss of 39.9%. When introducing the material into a tunable Ho3+/Pr3+ codoped ZBLAN fiber laser as a SA. stable Q-switched pulses with a tunable wavelength within 2.83-2.88 mu m were achieved. The largest output power of 30.8 mW, repetition rate of 78.12 kHz, and narrowest pulse width of 2.18 mu s were simultaneously attained when tuned to similar to 2.865 mu m at the pump power of 307.2 mW. while the largest pulse energy of 0.48 mu J was obtained at the longest tuning edge of 2.88 mu m. Our work indicates that LAR-GNRs are a type of versatile broadband SA material available for the mid-infrared region. (C) 2019 Optical Society of America under the terms of the OSA Open Access Publishing Agreement