Novel Two-Dimensional Ti3C2Tx MXenes/nano-carbon Sphere Hybrids for High-Performance Microwave Absorption

Binzhou Dai,Biao Zhao,Xi Xie,Tingting Su,Bingbing Fan,Rui Zhang,Rui Yang

DOI: https://doi.org/10.1039/c8tc01404c

IF: 6.4

2018-01-01

Journal of Materials Chemistry C

Abstract:Carbon spheres appeared for the first time during the process of etching Ti3AlC2 using hydrofluoric acid.

What problem does this paper attempt to address?

Novel Two-Dimensional Ti3C2TX/Ni-spheres Hybrids with Enhanced Microwave Absorption Properties

Ning Li,Xi Xie,Hongxia Lu,Bingbing Fan,Xiaohui Wang,Biao Zhao,Rui Zhang,Rui Yang

DOI: https://doi.org/10.1016/j.ceramint.2019.07.331

IF: 5.532

2019-01-01

Ceramics International

Abstract:Ti3C2Tx/Ni-spheres hybrids were successfully prepared through in situ hydrothermal assembly of Ni spheres on Ti3C2Tx layer, and then the electromagnetic wave absorbing materials were investigated in the range of 2-18 GHz. The as-synthesized Ti3C2Tx/Ni-spheres hybrids contain uniformly distributed Ni spheres on the edge of Ti3C2Tx layer and some of them enter the interspace between individual lamella. The Ti3C2Tx/Ni-spheres hybrids show an optimal reflection loss of -47.06 dB with the thickness of 1.5 mm at 12.4 GHz. The effective absorption bandwidth (EAB) reaches 3.6 GHz. The excellent electromagnetic wave absorbing properties can be explained in two ways. First is the conduction loss and dielectric loss of Ti3C2Tx and the second is the magnetic loss of Ni, in addition, the laminated structure could also enhance the microwave absorbing properties by the strong multi-reflections and scattering between MXene layers. The work of this article not only provides a new method for preparing novel electromagnetic wave absorbers, but also fine balance among small thickness, broad range band, and lightweight of the Ti3C2Tx/Ni-spheres hybrids, which makes Ti3C2Tx/Ni-spheres hybrids a promising materials for electromagnetic wave absorption application.
Embedment of Hollow SiO2 Spheres into Flower-Like Ti3C2Tx MXene Framework with Decoration of Carbon for Efficient Microwave Absorption

Sijia Wang,Ziying Zhang,Xuanxuan Fan,Yang Li,Jun Zhang,Longlong Xue,Shisheng Xiong

DOI: https://doi.org/10.1016/j.jallcom.2023.170724

IF: 6.2

2023-01-01

Journal of Alloys and Compounds

Abstract:With the advancement of modern microwave communication technologies, the development of lightweight absorption materials with high capacity and a wide absorption bandwidth has aroused great interest. Despite its low density, strong temperature resistance, high strength, and great electromagnetic energy storage capacity, SiO2 still has a long way to go in terms of efficiently dissipating microwaves due to its low polarization loss and conductive loss. Herein, the 3D sandwich-like M-Ti3C2Tx @SiO2 @C hybrids are syn-thesized by inserting SiO2 hollow spheres into the flower-like Ti3C2Tx MXene framework and decorating with carbon. SiO2 hollow spheres securely attached on monolayer Ti3C2Tx MXene nanosheets provide large electromagnetic energy storage capacity as well as additional interfacial polarization. The 3D flower-like Ti3C2Tx MXene framework and carbon coating ensure high conductive loss. The 3D sandwich-like M-Ti3C2Tx @SiO2 @C hybrids shows excellent microwave absorption performance. Under 40 wt% filler loadings, the 3D sandwich-like M-Ti3C2Tx @SiO2 @C hybrids deliver minimum reflection loss of - 43.97 dB at 4.5 mm thickness. At 1.5 mm thickness, their effective absorption band expands to 4.12 GHz. The facile and scalable synthesis strategy offers a novel design concept for the commercialization of high-performance microwave absorbers. & COPY; 2023 Elsevier B.V. All rights reserved.
High-Density Anisotropy Magnetism Enhanced Microwave Absorption Performance in Ti3C2Tx MXene@Ni Microspheres.

Caiyue Wen,Xiao Li,Ruixuan Zhang,Chunyang Xu,Wenbin You,Zhengwang Liu,Biao Zhao,Renchao Che

DOI: https://doi.org/10.1021/acsnano.1c08957

IF: 17.1

2021-01-01

ACS Nano

Abstract:Two-dimensional materials, especially the newly emerging MXene, have attracted numerous interests in the fields of energy conversion/storage and electromagnetic shielding/absorption. However, the inherently inevitable aggregation and absence of magnetic loss of MXene considerably limit its electromagnetic absorption application. The introduction of magnetic component and favorable structural engineering are the alternatives to improve the microwave absorption (MA) performance. Herein, we report a spheroidization strategy to assemble double-shell MXene@Ni microspheres, where the commonly lamellar MXene are reshaped into three-dimensional microspheres that provide the substrate for oriented growth of Ni nanospikes. Whereas this structural feature offers massive accessible active surfaces that effectively promote the dielectric loss ability, the introduction of magnetic Ni nanospikes enables the additional magnetic loss capacity. Benefiting from these merits, the synthesized 3D MXene@Ni microspheres exhibit superior MA performance with the minimum reflection loss value of -59.6 dB at an ultrathin thickness (∼1.5 mm) and effective absorption bandwidth of 4.48 GHz. Moreover, the electron holography results reveal that the high-density anisotropy magnetism plays an important role in the improvement of MA performance, which provides an insight for the design of MXene-based materials as high-efficient microwave absorbers.
Graphene-Wrapped Magnetic Multichamber Ti 3 C 2 T x Spheres for Stable Broadband Microwave Absorption

Wei Liu,Kun Jia,Tingting Yao,Lazhen Shen,Donghong Wang

DOI: https://doi.org/10.1021/acsami.4c10905

IF: 9.5

2024-09-15

ACS Applied Materials & Interfaces

Abstract:Two-dimensional transition metal carbides/nitrides (MXenes) have aroused widespread interest in the field of microwave absorption because of their unique layered structures. However, the inherent aggregation, poor impedance matching, and low chemical stability of MXenes inevitably obstruct their practical applications. Herein, a multichamber Fe(3)O(4)/Ti(3)C(2)T(x)@reduced graphene oxide (FT@RGO) hierarchical structure was constructed through self-assembly and sacrificial template strategies...

materials science, multidisciplinary,nanoscience & nanotechnology
Broadband High-Performance Microwave Absorption of the Single-Layer Ti3C2Tx MXene

Xuejiao Zhou,Junwu Wen,Zhenni Wang,Xiaohua Ma,Hongjing Wu

DOI: https://doi.org/10.1016/j.jmst.2021.11.029

2022-01-01

Journal of Material Science and Technology

Abstract:MXenes,a family of two-dimensional(2D)materials,exhibit peculiar microwave-absorbing behaviors due to their unique chemical composition and structure.Although laminated Ti3C2Tx MXenes with a multi-layer structure have been used for microwave absorption,real 2D MXenes with a single-layer structure have not yet been investigated.Here,the electromagnetic wave response behavior of single-layer Ti3C2Tx MXenes was explored in detail.The permittivity of Ti3C2Tx MXene rises dramatically with an increase in filler loading,and Ti3C2Tx MXene features a distinct dielectric response wherein dipolar polarization and interfacial polarization makes a greater contribution at low filler loading;conductive loss becomes more prominent at high filler loading.Versus laminated Ti3C2Tx MXene,single-layer Ti3C2Tx MXene delivers superior absorbing capability:The RLmin value of SL-Ti3C2Tx-22％reaches-43.5 dB at 6.5 GHz,and a broad EAB of 6.88 GHz can be attained at a thickness of 1.8 mm due to enhanced dipolar polarization,interfacial polarization,and conductive loss.This work is of great significance in guiding the future development of MXene-based absorbers.
Synthesis of CuS Nanoparticles Decorated Ti3C2Tx MXene with Enhanced Microwave Absorption Performance

Guangzhen Cui,Linbo Wang,Ling Li,Wei Xie,Guangxin Gu

DOI: https://doi.org/10.1016/j.pnsc.2020.06.001

IF: 4.269

2020-01-01

Progress in Natural Science Materials International

Abstract:MXene, a novel two-dimensional (2D) multi-layer material, has drawn unusual interest as the microwave absorbers for electromagnetic energy attenuation. Synthetic MXene-based heterostructure composites via optimizing structure is an effective strategy to endow MXene materials with high-performance microwave absorption. This study reports the fabrication and investigation of the microwave absorption performance of a sandwich-like CuS/Ti3C2Tx MXene composites prepared by loading CuS nanoparticles onto 2D Ti3C2Tx via a solvothermal method. The morphology and electromagnetic absorption properties of this composite were investigated and the results demonstrated that the CuS/Ti3C2Tx composite with a heterolayered architecture displayed superior microwave absorption ability. With a 35 wt% filler loading in the paraffin matrix, the minimum reflection loss value reached -45.3 dB at a frequency of 7.3 GHz and the effective absorption bandwidth achieved a value as high as 5.2 GHz with a thickness of 2.0 mm. The enhanced microwave absorption performances can be ascribed to the cooperation of the conductive network, interface polarization, dipole polarization, multiple reflection and scattering. Therefore, the synthesized CuS/Ti3C2Tx MXene composites offer an efficient foundation for the design and utilization of other lightweight microwave absorbers.
Three dimensional porous MXene/CNTs microspheres: Preparation, characterization and microwave absorbing properties

Yuhong Cui,Fei Wu,Jiqi Wang,Yabin Wang,Tariq Shah,Pei Liu,Qiuyu Zhang,Baoliang Zhang

DOI: https://doi.org/10.1016/j.compositesa.2021.106378

2021-06-01

Abstract:In this paper, a simple ultrasonic spray technology is used to assemble one-dimensional (1D) carboxylated carbon nanotubes (C-CNTs) and two-dimensional (2D) Ti3C2Tx MXene nanosheets into three-dimensional (3D) porous MXene/C-CNTs microspheres (MCM). After vacuum carbonization, C-MCM with excellent microwave absorbing properties are obtained. It finds that the synergy of MXene and CNTs makes C-MCM have good impedance matching and microwave attenuation capabilities. Under the best mass ratio (MXene: CNTs = 3:1) and filler content (30%), the minimum reflection loss (RLmin) is −45 GHz, and the corresponding matching thickness is 2.7 mm. When the thickness is 1.9 mm, the effective absorption bandwidth (EAB) reaches 4.9 GHz. By adjusting the thickness of the absorber, almost all electromagnetic waves in the C, X and Ku bands can be completely absorbed. Therefore, C-MCM provides a new way to manufacture electromagnetic wave absorbers with light weight, thin thickness, high efficiency and broadband.
2D Ti3C2T MXene/MOFs composites derived CoNi bimetallic nanoparticles for enhanced microwave absorption

Zhikang Liu,Jin Chen,Meidan Que,Huiqi Zheng,Lingfu Yang,Hudie Yuan,Yuzhao Ma,Yanjun Li,Xiaofeng Yang

DOI: https://doi.org/10.1016/j.cej.2022.138442

IF: 15.1

2022-12-01

Chemical Engineering Journal

Abstract:The emerging two-dimensional (2D) transition metal carbide (MXene) has been a hot topic due to its special structure and high dielectric loss. However, the inevitable stacking phenomenon and lack of magnetic loss of the related MXene materials seriously restrict their application in electromagnetic (EM) absorption. Herein, Ti3C2T x (a typical material of MXene family) modified with metal–organic frameworks (MOFs) is prepared via simple electrostatic self-assembly and consequent heat treatment. The lamellar MXene provided the substrate for anchoring the MOFs, and the Ni nanoparticles catalytically derived carbon nanofibers (CNFs) served as bridges to construct the cross-linked network. Based on this network structure, the extensive heterogeneous interfaces effectively facilitate the dielectric loss ability, and the addition of magnetic CoNi nanoparticles can enhance the additional magnetic loss capacity. It is worth noting that when the matching thickness is only 1.76 mm, the minimum reflection loss (RLmin) value of the sample (Ti3C2T x /CNFs/TiO2/CoNi) reaches –54.6 dB, and the corresponding effective absorption bandwidth (EAB, RL < –10 dB) is 4.0 GHz (11.9–15.9 GHz). These results show that magnetic-dielectric synergistic, interfacial polarization, and multilayer structure, were conducive to the improvement of microwave absorption (MA) properties. This study envisions a novel strategy for constructing efficient MXene-based microwave absorbers.

engineering, chemical, environmental
Electrostatic-spinning Construction of HCNTs@Ti3C2Tx MXenes Hybrid Aerogel Microspheres for Tunable Microwave Absorption

Ying Li,Siren Guo,Yudi Li,Kaiyou Wu,Linlin Zhao,Xi Liu,Xulin Yang,Pan Wang,Yuxin Yang,Yan Sun,Zihao Mou

DOI: https://doi.org/10.1515/rams-2023-0339

2023-01-01

REVIEWS ON ADVANCED MATERIALS SCIENCE

Abstract:Helical carbon nanotubes (HCNTs) are chiral materials that can form an induced magnetic field when current passes through them, making them a desirable material for absorbing microwaves. However, poor electrical properties and inert surfaces limit the application of HCNTs as sole materials. In this study, we develop HCNTs@Ti3C2Tx MXenes hybrid aerogel microspheres synthesized using an electrospinning-assisted ice template method. The modified surfaces of the HCNTs form hydrogen bonds with Ti3C2Tx MXenes to produce hybrid aerogel microspheres. Because of the different functionalized surfaces of HCNTs (F-HCNTs), F-HCNTs@Ti3C2Tx MXenes could be adjusted to obtain effective reflection loss (RL) of microwaves ranging from 2 to 18 GHz. The observed advantageous RL is attributed to the modified surface of the HCNTs, their porous structure, and the optimized impedance matching derived from the synergistic effect between HCNTs and Ti3C2Tx MXenes. Successful assembly method for the 3D architectures of HCNTs@Ti3C2Tx MXenes hybrid aerogel microspheres significantly widens the practical applications of HCNTs in microwave absorption.
3D Ti3C2Tx MXene/C Hybrid Foam/epoxy Nanocomposites with Superior Electromagnetic Interference Shielding Performances and Robust Mechanical Properties

Lei Wang,Hua Qiu,Ping Song,Yali Zhang,Yuanjin Lu,Chaobo Liang,Jie Kong,Lixin Chen,Junwei Gu

DOI: https://doi.org/10.1016/j.compositesa.2019.05.030

IF: 9.463

2019-01-01

Composites Part A Applied Science and Manufacturing

Abstract:Few-layered Ti3C2Tx MXene was prepared by ionic intercalation and sonication-assisted method. Porous three-dimensional (3D) Ti3C2Tx MXene/C hybrid foam (MCF) was fabricated by sol-gel followed by thermal reduction. The MCF/epoxy EMI shielding nanocomposites were obtained via vacuum-assisted impregnation followed by curing process. When the mass fraction of MCF was 4,25 wt% (MCF-5), the MCF-5/epoxy EMI shielding nano composites exhibited the optimal electrical conductivity of 184 S/m and the maximum EMI SE of 46 dB, 3.1 x 10(4) and 4.8 times higher than that of MCF-0/epoxy nanocomposites (without Ti3C2T MXene), respectively. Furthermore, the corresponding Young's modulus of 3.96 GPa and hardness of 0.31 GPa was increased by 13% and 11%, respectively. Conductive networks can realize the attenuation and dissipation of electromagnetic waves by multiple reflection & reabsorption, and absorption is main shielding mechanism. Unique 3D conductive networks of MCF would expand wider application of the Ti3C2T MXene/polymer-based nanocomposites in high-tech EMI shielding fields.
Ni-MOF/Ti3C2Tx derived multidimensional hierarchical Ni/TiO2/C nanocomposites with lightweight and efficient microwave absorption

Meng Wang,Panpan Zhou,Tong Feng,Zhi Song,Qingguo Ren,Huidong Gu,Xueqing Shi,Qitu Zhang,Lixi Wang

DOI: https://doi.org/10.1016/j.ceramint.2022.03.154

IF: 5.532

2022-01-01

Ceramics International

Abstract:Benefiting from its large specific surface area, abundant defects and functional groups, two-dimensional (2D) laminated Ti3C2Tx MXene is a kind of electromagnetic wave (EMW) absorber with great potential. However, the impedance mismatch caused by the excessive conductivity, inappropriate permittivity and lack of magnetic loss seriously hinders the application of MXene to EMW absorption. Herein, multidimensional hierarchical Ni/TiO2/C nanocomposites composed of three-dimensional (3D) hydrangea-like Ni/C microspheres and well-arranged 2D carbon sheets embedded with TiO2 nanoparticles were successfully fabricated from a Ni-based trimellitic acid framework (Ni-BTC) and Ti3C2Tx MXene via facile in-situ solvothermal assembly and annealing processes. As expected, excellent EMW absorption properties were obtained only by changing the annealing temperature. The minimum reflection loss (RLmin) value of -45.6 dB and the effective absorption bandwidth (EAB) of 3.40 GHz (14.6-18.0 GHz) with a layer thickness of only 1.5 mm is obtained by annealing the sample at 700 degrees C. The outstanding ternary multilayer structure and the optimization of magnetoelectric synergy in impedance matching jointly create its remarkable EMW absorption performance. This work is expected to provide a simple and effective method to design MXene-based EMW absorbing materials possessing high absorption intensity, light weight, wide EAB and thin thickness.
Synthesis and Microwave Absorption of Ti3C2Tx MXene with Diverse Reactant Concentration, Reaction Time, and Reaction Temperature

Guangzhen Cui,Xin Zheng,Xuliang Lv,Qi Jia,Wei Xie,Guangxin Gu

DOI: https://doi.org/10.1016/j.ceramint.2019.08.071

IF: 5.532

2019-01-01

Ceramics International

Abstract:MXene materials with efficient electromagnetic (EM) microwave absorber applications are in high demand. Herein, the EM wave absorption properties of two-dimensional MXene Ti3C2Tx, fabricated by etching the Ti3AlC2 phase with an enchant of HCl and LiF, was thoroughly investigated over a frequency range of 2-18 GHz. In addition, the impact of three critical factors (reactant concentration, reaction time, and reaction temperature) on the morphology control and dielectric properties was discussed. With increasing degree of exfoliation, the multilayer structure of Ti3C2Tx changed gradually, thereby further influencing the microwave absorption properties. Among the etched samples, Ti3C2Tx prepared with 9 M HCl at 35 degrees C for 24 h exhibited an excellent reflection loss of -40.8 dB at 13.9 GHz with a thickness of 1.45 mm, while also possessed the broadest effective bandwidth, reaching 3.66 GHz at 1.68 mm. The demonstrated EM wave response mechanism, indicated that the conduction loss and polarization loss contribute significantly to the EM wave absorption performance. These findings endow the Ti3C2Tx material with an effective foundation for the construction of novel EM wave absorbers.
CeO2/Ti3C2Tx MXene Nanostructures for Microwave Absorption

Zhiwei Liu,Yan Zhao,Shuang Li,Tianpei Sun,Hansong Liu,Kai Wang,Xiangbao Chen

DOI: https://doi.org/10.1021/acsanm.2c00829

IF: 6.14

2022-01-01

ACS Applied Nano Materials

Abstract:In this paper, a two-dimensional MXene loaded with CeO2 nanoparticles was successfully synthesized through a simple solvothermal sintering method. The nanocomposite obtained by mixing the CeO2/Ti3C2Tx MXene with paraffin at 30 wt % has a high reflection loss of -47.27 dB at a thickness of 1.9 mm and an effective absorption bandwidth of up to 4.22 GHz which is higher than that of a similar absorbing system. By adjusting the composition ratio and the thickness of the system, almost all S, C, X, and Ku bands can be covered. Its excellent performance benefits from the abundant oxygen vacancies brought by CeO2 nanoparticles in which Ce3+ and Ce4+ ions coexist and the rich microinterfaces brought by the CeO2-C-Ti3C2Tx sandwich structure. In addition, CeO2/Ti3C2Tx MXene nanocomposites also have high thermal stability. This research extends the thought on the design of high-performance microwave-absorbing materials.
Hydrothermal assembly of NiCoAI/Ti 3 C 2 T x MXene composites for tunable microwave absorption

Tongtong Xu,Jun Li,Zhenyu Shen,Wenwen Xing,Zhongxiang Zhou

DOI: https://doi.org/10.1109/ISAPE54070.2021.9752793

2021-01-01

Abstract:Herein, a new type tunable microwave absorber of NiCoAl/Ti3C2Tx MXene was proposed and synthesized via a simple hydrothermal method. The scanning electron microscopy confirmed that the NiCoAl is of high quality with flower-like structure uniformly bonded on the laminar Ti3C2Tx surface. The dielectric properties of the samples in X-band frequency were studied, and their microwave absorpt...
Hierarchical Ti3 C2 Tx MXene/Carbon Nanotubes Hollow Microsphere with Confined Magnetic Nanospheres for Broadband Microwave Absorption

Chang Zhang,Zhengchen Wu,Chunyang Xu,Bintong Yang,Lei Wang,Wenbin You,Renchao Che

DOI: https://doi.org/10.1002/smll.202104380

IF: 13.3

Small

Abstract:Hierarchical hollow structure with unique interfacial properties holds great potential for microwave absorption (MA). Ti3 C2 Tx MXene has been a hot topic due to rich interface structure, abundant defects, and functional groups. However, its overhigh permittivity and poor aggregation-resistance limit the further application. Herein, a hierarchical MXene-based hollow microsphere is prepared via a facile spray drying strategy. Within the microsphere, few-layered MXene nanosheets are separated by dispersed carbon nanotubes (CNTs), exposing abundant dielectric polarization interfaces. Besides, numerous magnetic Fe3 O4 nanospheres are uniformly dispersed and confined within nano-cavities between 1D network and 2D framework. Such a novel structure simultaneously promotes interfacial polarization by ternary MXene/CNTs/Fe3 O4 interfaces, enhances magnetic loss by microscale and nanoscale coupling network, enlarges conduction loss by MXene/CNTs dual-network, and optimizes impedance matching by hierarchical porous structure. Therefore, Fe3 O4 @Ti3 C2 Tx /CNTs composite achieves excellent MA property with a maximum reflection loss of -40.1 dB and an effective bandwidth of 5.8 GHz at the thickness of only 2 mm. This work demonstrates a feasible hierarchical structure design strategy for multi-dimension MXene composite to realize the high-efficiency MA performance.
In situ growing CNTs/TiO 2 heterojunction on MXene sheets for enhanced microwave absorption via multiple electron transfer paths and polarization

Jing Zhang,Jin Chen,Zhikang Liu,Yuzhao Ma,XinLe Wang,Xiaofeng Yang,Meidan Que,Yanjun Li

DOI: https://doi.org/10.1016/j.ceramint.2023.10.349

IF: 5.532

2023-12-04

Ceramics International

Abstract:The novel two-dimensional Ti 3 C 2 T x material exhibits great potential for microwave absorption owing to its 2D layered graphene-like structure and unique physical properties. However, the limited release of absorbing properties due to the low dielectric loss of Ti 3 C 2 T x and its single loss mechanism pose challenges in meeting the functional requirements for microwave absorbers. Herein, carbon nanotubes (CNTs) were grown on the Ti 3 C 2 T x substrates in a tip growth mode under the catalytic influence of Ni using the in situ induced method. Consequently, Ti 3 C 2 T x /CNTs/TiO 2 (TCT) structures were successfully prepared through carbonization conditions. It is worth noting that the composite material TCT-800 exhibits excellent absorption performance. The minimum reflection loss (RL min ) value reaches −44.6 dB when the matching thickness is only 1.4 mm, and the corresponding effective absorption bandwidth (EAB, RL < −10 dB) spans from 11.9 GHz to 15.9 GHz, totaling a range of 4.2 GHz. The excellent electromagnetic wave absorption performance of TCT-800 composites is attributed to the polarization phenomenon of more heterogeneous interfaces constructed by Ti 3 C 2 T x nanosheets, CNTs, and TiO 2 nanoparticles. This work provides a strategy for synthesizing Ti 3 C 2 T x -based composites with strong electromagnetic attenuation and wide absorption bandwidth performance.

materials science, ceramics
Effect of Crystal Transformation on the Intrinsic Defects and the Microwave Absorption Performance of Mo2TiC2Tx/RGO Microspheres

Mengyun Ling,Feijie Ge,Fei Wu,Lei Zhang,Qiuyu Zhang,Baoliang Zhang

DOI: https://doi.org/10.1002/smll.202306233

IF: 13.3

2023-10-19

Small

Abstract:The 3D Mo2TiC2Tx‐based microspheres are first constructed. Mo2TiC2Tx/RGO with wrinkled morphology are first applied to the microwave absorption field. The effects of carbonization temperature on its internal crystal structure and intrinsic defects are systematically investigated, and the structure–activity relationships are deeply explored. The RLmin exceeds −55.1 dB and effective absorption bandwidth covers 5.7 GHz at 15% filler loading. The nitrides and carbides of transition metals are highly favored due to their excellent physical and chemical properties, among which MXene is a hot research topic for microwave absorption. Herein, the controlled preparation of 3D Mo2TiC2Tx‐based microspheres toward microwave absorption is reported for the first time. With the merits of the performances of both reduced graphite oxide (RGO) and MXene sufficiently considered, the influence of carbonization temperature on the internal crystal structure and the effective microwave‐material interaction surface of the prepared Mo2TiC2Tx/RGO is systematically investigated. The structure–activity relationships relating the apparent morphology and crystal structure to the microwave absorption performance are deeply explored, and the wave absorption mechanism is put forward as well. The results show that the Mo2TiC2Tx/RGO‐700 product obtained after heating treatment at 700 °C exhibits excellent microwave absorption performance, with the RLmin being up to −55.1 dB@2.1 mm@13.8 GHz, and the corresponding effective absorption bandwidth covering 5.7 GHz. The outstanding microwave absorption characteristics are attributed to the appropriate impedance matching, high specific surface area, rich intrinsic defects, desirable conductivity, and strong multipolarization capabilities. This work enriches the types of MXene‐based composite absorbers and provides a new strategy for controlled preparation of high‐performance 3D composite absorbers.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology
CeO 2 /Ti 3 C 2 T x MXene Nanostructures for Microwave Absorption

Zhiwei Liu,Yan Zhao,Shuang Li,Tianpei Sun,Hansong Liu,Kai Wang,Xiangbao Chen

DOI: https://doi.org/10.1021/acsanm.2c00829

IF: 6.14

2022-04-05

ACS Applied Nano Materials

Abstract:In this paper, a two-dimensional MXene loaded with CeO2 nanoparticles was successfully synthesized through a simple solvothermal sintering method. The nanocomposite obtained by mixing the CeO2/Ti3C2Tx MXene with paraffin at 30 wt % has a high reflection loss of −47.27 dB at a thickness of 1.9 mm and an effective absorption bandwidth of up to 4.22 GHz which is higher than that of a similar absorbing system. By adjusting the composition ratio and the thickness of the system, almost all S, C, X, and Ku bands can be covered. Its excellent performance benefits from the abundant oxygen vacancies brought by CeO2 nanoparticles in which Ce3+ and Ce4+ ions coexist and the rich microinterfaces brought by the CeO2–C–Ti3C2Tx sandwich structure. In addition, CeO2/Ti3C2Tx MXene nanocomposites also have high thermal stability. This research extends the thought on the design of high-performance microwave-absorbing materials.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsanm.2c00829.Additional experimental data and mechanistic analysis (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology
3D Ultralight Hollow NiCo Compound@MXene Composites for Tunable and High-Efficient Microwave Absorption

Hui-Ya Wang,Xiao-Bo Sun,Shu-Hao Yang,Pei-Yan Zhao,Xiao-Juan Zhang,Guang-Sheng Wang,Yi Huang

DOI: https://doi.org/10.1007/s40820-021-00727-y

2021-01-01

Abstract:Abstract The 3D hollow hierarchical architectures tend to be designed for inhibiting stack of MXene flakes to obtain satisfactory lightweight, high-efficient and broadband absorbers. Herein, the hollow NiCo compound@MXene networks were prepared by etching the ZIF 67 template and subsequently anchoring the Ti 3 C 2 T x nanosheets through electrostatic self-assembly. The electromagnetic parameters and microwave absorption property can be distinctly or slightly regulated by adjusting the filler loading and decoration of Ti 3 C 2 T x nanoflakes. Based on the synergistic effects of multi-components and special well-constructed structure, NiCo layered double hydroxides@Ti 3 C 2 T x (LDHT-9) absorber remarkably achieves unexpected effective absorption bandwidth (EAB) of 6.72 GHz with a thickness of 2.10 mm, covering the entire Ku-band. After calcination, transition metal oxide@Ti 3 C 2 T x (TMOT-21) absorber near the percolation threshold possesses minimum reflection loss (RL min ) value of − 67.22 dB at 1.70 mm within a filler loading of only 5 wt%. This work enlightens a simple strategy for constructing MXene-based composites to achieve high-efficient microwave absorbents with lightweight and tunable EAB."Image missing"

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology
Elaborately Designed 3D Honeycomb M-Ti3C2Tx@MoS2@C Heterostructures As Advanced Microwave Absorbers

Xuanxuan Fan,Ziying Zhang,Sijia Wang,Jun Zhang,Shisheng Xiong

DOI: https://doi.org/10.1016/j.apsusc.2023.157116

IF: 6.7

2023-01-01

Applied Surface Science

Abstract:Microwave absorption materials with lightweight, high absorption performance, and a broad absorption bandwidth are becoming increasingly popular due to the rapid advancements in wearable devices and portable electronic products. The two-dimensional Ti3C2Tx MXene is a highly promising electromagnetic shielding material thanks to its excellent conductivity, rich functional groups and customizable surface chemistry. However, the low dielectric loss of this material restricts its applications in microwave absorption. Herein, 3D honeycomb M- Ti3C2Tx@MoS2@C heterostructures were synthesized by simple hydrothermal and secondary annealing methods. Vertically assembled MoS2 nanosheets ensured a large electromagnetic energy storage capacity and promoted additional interfacial polarization. The honeycomb surface structure facilitated the electromagnetic wave attenuation through multiple reflections. The carbon coating and M- Ti3C2Tx matrix resulted in high conductive loss in the final products. The three-dimensional honeycomb M- Ti3C2Tx@MoS2@C heterostructures demonstrated exceptional microwave absorption performance. When filler loadings reached 40 wt%, the 3D honeycomb M- Ti3C2Tx@MoS2@C heterostructures delivered a minimum reflection loss of -47.55 dB at a thickness of 4.0 mm, with the added benefit of increasing the effective absorption bandwidth to 4.02 GHz. These findings paved the way for the commercialization of advanced microwave absorbers.

Novel Two-Dimensional Ti3C2Tx MXenes/nano-carbon Sphere Hybrids for High-Performance Microwave Absorption

Novel Two-Dimensional Ti3C2TX/Ni-spheres Hybrids with Enhanced Microwave Absorption Properties

Embedment of Hollow SiO2 Spheres into Flower-Like Ti3C2Tx MXene Framework with Decoration of Carbon for Efficient Microwave Absorption

High-Density Anisotropy Magnetism Enhanced Microwave Absorption Performance in Ti3C2Tx MXene@Ni Microspheres.

Graphene-Wrapped Magnetic Multichamber Ti 3 C 2 T x Spheres for Stable Broadband Microwave Absorption

Broadband High-Performance Microwave Absorption of the Single-Layer Ti3C2Tx MXene

Synthesis of CuS Nanoparticles Decorated Ti3C2Tx MXene with Enhanced Microwave Absorption Performance

Three dimensional porous MXene/CNTs microspheres: Preparation, characterization and microwave absorbing properties

2D Ti3C2T MXene/MOFs composites derived CoNi bimetallic nanoparticles for enhanced microwave absorption

Electrostatic-spinning Construction of HCNTs@Ti3C2Tx MXenes Hybrid Aerogel Microspheres for Tunable Microwave Absorption

3D Ti3C2Tx MXene/C Hybrid Foam/epoxy Nanocomposites with Superior Electromagnetic Interference Shielding Performances and Robust Mechanical Properties

Ni-MOF/Ti<sub>3</sub>C<sub>2</sub>T<i><sub>x</sub></i> derived multidimensional hierarchical Ni/TiO<sub>2</sub>/C nanocomposites with lightweight and efficient microwave absorption

Synthesis and Microwave Absorption of Ti3C2Tx MXene with Diverse Reactant Concentration, Reaction Time, and Reaction Temperature

CeO2/Ti3C2Tx MXene Nanostructures for Microwave Absorption

Hydrothermal assembly of NiCoAI/Ti 3 C 2 T x MXene composites for tunable microwave absorption

Hierarchical Ti3 C2 Tx MXene/Carbon Nanotubes Hollow Microsphere with Confined Magnetic Nanospheres for Broadband Microwave Absorption

In situ growing CNTs/TiO 2 heterojunction on MXene sheets for enhanced microwave absorption via multiple electron transfer paths and polarization

Effect of Crystal Transformation on the Intrinsic Defects and the Microwave Absorption Performance of Mo2TiC2Tx/RGO Microspheres

CeO 2 /Ti 3 C 2 T x MXene Nanostructures for Microwave Absorption

3D Ultralight Hollow NiCo Compound@MXene Composites for Tunable and High-Efficient Microwave Absorption

Elaborately Designed 3D Honeycomb M-Ti3C2Tx@MoS2@C Heterostructures As Advanced Microwave Absorbers