Strength‐Ductility Synergy in an Austenitic Stainless Steel Processed by Warm Rolling and Subsequent Cryogenic Treatment
Liu Zhan,Guo Yanhui,Cui Mingzhe,Pang Linghuan,Liu Xin,Fu Bin
DOI: https://doi.org/10.1002/srin.202400747
IF: 2.1258
2024-12-05
steel research international
Abstract:The warm‐rolled and cryogenically treated sample achieved exceptional mechanical properties, with a yield strength of ≈949 MPa and elongation of ≈56.2%. Its high strength stems from grain refinement, increased dislocation density, and martensite formation via cryogenic treatment. Deformation is stage‐dependent: early dislocation slip, mid‐stage transformation‐induced plasticity (TRIP) effect, and late‐stage martensite slip. Fine grains delay TRIP, enhancing ductility. The austenitic stainless steel undergo warm rolling, followed by cryogenic treatment. The warm‐rolled and cryogenically treated (WR‐CT) sample exhibits superior strength and ductility compared to the warm‐rolled (WR) sample, achieving a yield strength of 949 MPa and an elongation of ≈56.2%. The enhanced strength is attributed to the higher dislocation density, additional grain refinement, and the presence of martensite in the WR‐CT sample. The WR and WR‐CT samples exhibit similar deformation mechanisms. In the initial stage, dislocation slip predominantly governs the deformation. During the intermediate stage, the transformation‐induced plasticity (TRIP) effect dominates the deformation mechanism. In the final stage, nearly all austenite transforms into martensite, and deformation mainly occurs via dislocation slip within the martensite phase. However, in the WR‐CT sample, the TRIP effect is delayed during the stable processing stage (≈8–23%) due to the higher mechanical stability of austenite, resulting from further grain refinement and higher dislocation density. Additionally, the coordinated deformation of strain‐induced martensite with varying orientations contributes to delayed necking, achieving an optimal balance between strength and ductility.
metallurgy & metallurgical engineering