Abstract:Ni/Co(OH)2 nanosheets were prepared through an electroconversion reaction with CoCl2.6 H2O and NiCl2.6 H2O as raw materials and without an added structural guiding agent. NiCo2O4 was obtained by calcination with Ni/Co(OH)2 as a precursor. The structure and morphology of Ni/Co(OH)2 and NiCo2O4 were characterized by XRD, FTIR, XPS, and SEM. The characterization results show that the particle size range of Ni/Co(OH)2 with a three-dimensional nanostructure is 10–84 nm, and it is formed by staggered stacking of nanosheets with a thickness of approximately 19 nm. The electrochemical test results show that the specific capacitance of the Ni/Co(OH)2 nanosheet electrode in 1 M KOH electrolyte and 1 A/g current density is as high as 908.33 F/g, which can be attributed to its unique three-dimensional nanolayered structure, and as a result, more redox reaction active sites can be provided in the charge storage process. In addition, the structure of the Ni/Co(OH)2 nanosheet electrode can slow down the volume change during the charge–discharge cycle and maintain the stability of the structure. Under the high current density of 10 A/g, the specific capacitance retention rate is 71% at 1500 cycles and 74% at 3500 cycles, but then it shows a downwards trend. The capacitance retention rate fluctuates between 60% and 30%. After 10000 cycles, the specific capacitance retention rate is still 30%, indicating that the electrode exhibits a good cycle performance.

Electrochemical Properties of NiCoO2 Synthesized by Hydrothermal Method

Characterization of NiCo2 O4 as high-performance supercapacitor electrode materials

Morphology and electrochemical properties of NiCo2O4 powders prepared by a facile hydrothermal method

Hydrothermal and Soft-Templating Synthesis of Mesoporous NiCo2O4 Nanomaterials for High-Performance Electrochemical Capacitors

Facilely synthesized porous NiCo2O4 flowerlike nanostructure for high-rate supercapacitors

Facilely Synthesized Α Phase Nickel–cobalt Bimetallic Hydroxides: Tuning the Composition for High Pseudocapacitance

Design and synthesis of nitrogen-doped hexagonal NiCoO nanoplates derived from Ni-Co-MOF for high-performance electrochemical energy storage

High-Performance Ni-Co Sulfide Nanosheet-Nanotubes Grown on Ni Foam As a Binder Free Electrode for Supercapacitors

NiCo2O4 Particles with Diamond-Shaped Hexahedron Structure for High-Performance Supercapacitors

Micro-Spatial Hydrothermal Preparation of Nitrogen-doped Carbon/NiCo2S4 Electrode Material for Supercapacitors

Electroconversion synthesis of Ni/Co layered nanomaterials for high-performance supercapacitors

Facile hydrothermal synthesis of urchin‐like NiCo 2 O 4 as advanced electrochemical pseudocapacitor materials

Effect of Hydrothermal Method Temperature on the Spherical Flowerlike Nanostructures NiCo(OH)4-NiO

Sodium Dodecyl Sulfate-Assisted Synthesis of Flower-Like NiCo2O4 Microspheres with Large Specific Surface Area for Supercapacitors

Synthesis of Co–Ni Oxides @ CNTs Nanoflowers and Their Electrochemical Performance in Supercapacitors

Preparation of electrochemical supercapacitor based on fluffy sphere-like NiCoCu-carbonate hydroxide

Reagent-assisted hydrothermal synthesis of NiCo 2 O 4 nanomaterials as electrodes for high-performance asymmetric supercapacitors

The Design and Synthesis of NiCoO2@NiCoO2@Ni Nanoflakes Arrays for Electrochemical Energy Storage

3D net-like Co3O4@NiO nanostructures for high performance supercapacitors

Facile and Large-Scale Chemical Synthesis of Highly Porous Secondary Submicron/micron-Sized NiCo2O4 Materials for High-Performance Aqueous Hybrid AC-NiCo2O4 Electrochemical Capacitors

Nanorod NiMoO4@NiCo2S4 as an advanced electrode material for high-performance supercapacitors