Abstract:In this study, Pt nanoparticles-loaded nitrogen-doped mesoporous carbon nanotube (Pt/NMCT) was successfully synthesized through a polydopamine-mediated “one-pot” co-deposition strategy. The Pt source was introduced during the co-deposition of polydopamine and silica on the surface of SiO2 nanowire (SiO2 NW), and Pt atoms were fixed in the skeleton by the chelation of polydopamine. Thus, in the subsequent calcination process in nitrogen atmosphere, the growth and agglomeration of Pt nanoparticles were effectively restricted, achieving the in situ loading of uniformly dispersed, ultra-small (~2 nm) Pt nanoparticles. The method is mild, convenient, and does not require additional surfactants, reducing agents, or stabilizers. At the same time, the use of the dual silica templates (SiO2 NW and the co-deposited silica nanoclusters) brought about a hierarchical pore structure with a high specific surface area (620 m2 g−1) and a large pore volume (1.46 cm3 g−1). The loading process of Pt was studied by analyzing the electron microscope and X-ray photoelectron spectroscopy of the intermediate products. The catalytic performance of Pt/NMCT was investigated in the reduction of 4-nitrophenol. The Pt/NMCT with a hierarchical pore structure had an apparent reaction rate constant of 0.184 min−1, significantly higher than that of the sample, without the removal of the silica templates to generate the hierarchical porosity (0.017 min−1). This work provides an outstanding contribution to the design of supported noble metal catalysts and also highlights the importance of the hierarchical pore structure for catalytic activity.

One-Pot Synthesis Of Ni Nanoparticle/Ordered Mesoporous Carbon Composite Electrode Materials For Electrocatalytic Reduction Of Aromatic Ketones

Co-modified Ni/N-doped Carbon As Electrocatalysts for HER and OER

Facile Synthesis of Porous Dendritic Bimetallic Platinum-Nickel Nanocrystals As Efficient Catalysts for the Oxygen Reduction Reaction

Highly Efficient and Self-Supported 3D Carbon Nanotube Composite Electrode for Enhanced Oxygen Reduction Reaction

One-step Chemical Vapor Synthesis of Ni/graphene Nanocomposites with Excellent Electromagnetic and Electrocatalytic Properties

Rapid one-step synthesis and electrochemical performance of nio/ni with tunable macroporous architectures

Ni-Co Alloy Nanoparticles Catalyze Selective Electrochemical Coupling of Nitroarenes into Azoxybenzene Compounds in Aqueous Electrolyte.

One-pot Synthesis of PtRu Nanodendrites As Efficient Catalysts for Methanol Oxidation Reaction.

Size Controllable Metal Nanoparticles Anchored on Nitrogen Doped Carbon for Electrocatalytic Energy Conversion

Facile One‐Pot, One‐Step Synthesis of a Carbon Nanoarchitecture for an Advanced Multifunctonal Electrocatalyst

Directly Anchoring Fe3C Nanoclusters and FeNx Sites in Ordered Mesoporous Nitrogen-Doped Graphitic Carbons to Boost Electrocatalytic Oxygen Reduction

One-pot synthesis of NiFe foam-supported FeWO4/Ni3Se2 nanocomposites and their enhanced electrocatalytic performance for oxygen evolution reaction

Facile One-Pot Synthesis of Binder-Free Nano/micro Structured Dendritic Cobalt Activated Nickel Sulfide: a Highly Efficient Electrocatalyst for Oxygen Evolution Reaction

In-situ CVD Synthesis of Ni@N-CNTs/carbon Paper Electrode for Electro-Reduction of CO2

Self-templated Synthesis of Novel Carbon Nanoarchitectures for Efficient Electrocatalysis

One-pot Synthesis of Mesoporous Palladium/c Nanodendrites As High-Performance Oxygen Reduction Eletrocatalysts Through a Facile Dual Surface Protecting Agent-Assisted Strategy

CuNi alloy nanoparticles embedded in N-doped carbon framework for electrocatalytic reduction of CO2 to CO

Controllable Synthesis of Mesoporous Carbon Nanospheres and Fe-N/Carbon Nanospheres As Efficient Oxygen Reduction Electrocatalysts

One-Pot Synthesis of Ultra-Small Pt Nanoparticles-Loaded Nitrogen-Doped Mesoporous Carbon Nanotube for Efficient Catalytic Reaction

Facile synthesis of Co–Fe layered double hydroxide nanosheets wrapped on Ni-doped nanoporous carbon nanorods for oxygen evolution reaction

Atomically dispersed Ni anchored on polymer-derived mesh-like N-doped carbon nanofibers as an efficient CO2 electrocatalytic reduction catalyst