Topotactic Reduction Toward a Noncentrosymmetric Deficient Perovskite Tb0.50Ca0.50Mn0.96O2.37 with Ordered Mn Vacancies and Piezoelectric Behavior

Hao Zhang,Song Gao,Qinghua Zhang,Jingen Wu,Jie Liang,Cheng Dong,Lin Gu,Shuxiang Dong,Junliang Sun,Fuhui Liao,Jianhua Lin,Ruqiang Zou,Guobao Li

DOI: https://doi.org/10.1021/acs.chemmater.7b04115

IF: 10.508

2017-01-01

Chemistry of Materials

Abstract:Low-temperature reduction of perovskite Tb0.5Ca0.5MnO3-x yields novel crystal-structured noncentrosymmetric compound Tb0.50Ca0.50Mn0.962.33+O2.37, which unusually crystallizes in cubic lattice I23 (a similar to 15.27 angstrom) based on a 4a(p) x 4a(p) x 4a(p) expansion relative to the simple cubic perovskite unit cell. Rietveld refinements and HAADF-STEM images are used for the structure determination, revealing a rare-typed metal-anion coordination framework which consists of corner-shared tetrahedra and pyramids, and edge-shared bipyramids and octahedra. 2/64 B-site Mn-ordered vacancies are observed for the first time acting as the apex and body center of the I lattice in reduced systems. Room-temperature piezoelectricity is detected, with a quasistatic d(33) value of similar to 0.32 pC N-1 and inverse d(33) value of similar to 10.5 pm V-1. This phase primarily exhibits antiferromagnetic ordering below T-N similar to 70 K, with ferromagnetic responses resulted from spin-canting below 40 K. This work provides a new way toward synthesizing unconventional acentric materials, in the absence of second-order Jahn-Teller active "distortion centers".