Synthesis of Redox-Active Dendronized Poly(ferrocenylsilane) and Application As High-Performance Supercapacitors

Zhiyu Cheng,Lirong Cai,Yongfu Qiu,Xueyi Chang,Hongbo Fan,Biye Ren

DOI: https://doi.org/10.1016/j.jorganchem.2017.10.002

IF: 2.345

2017-01-01

Journal of Organometallic Chemistry

Abstract:A novel dendronized poly(ferrocenylsilane) (PFS-D) is prepared by ionic self-assembly of cationic poly(ferrocenylsilane) of [Fe(eta-C5H4)(2)SiMe- (OCH2CH2NMe3I)](n) (PFS) with anionic dendrons of 3,4,5-tris(n-octane-1-yloxy)- benzoic acid [(3,4,5)8G1-COOK]. XRD profiles and POM indicated the presence of the liquid crystalline phase in the PFS-D at room temperature that is resulted from the dendritic amphiphiles, which formed the end-to-end bilayer lamellar structure with the long period d = 3.27 nm. PFS-D coated on Ni foam (PFS-D/Ni) was applied as electrode materials for supercapacitors. CV measurements indicated that PFS-D/Ni exhibited a good reversible redox process and this observation was deemed to originate from its ferrocenyl moieties in liquid crystalline phase. The as-prepared PFS-D/Ni possessed a specific capacitance as high as 197 F g(-1) calculated from discharge curve with current density 5 A g(-1). The long-term cycle life stability for PFS-D/Ni was examined and the results showed that the capacitance decay was similar to 14% over 3000 cycles, indicating its long cycle life. Furthermore, they could also be used to assemble a simple solid-state supercapacitor. In a word, the PFS-D/Ni was reported as a promising electrode material for efficient pseudo-capacitors for the first time. (C) 2017 Elsevier B.V. All rights reserved.