Abstract:In this paper, an MoOx film is deposited on a polyethylene terephthalate (PET) substrate as a buffer layer to improve the surface roughness of the flexible PET substrate. With an optimized MoOx thickness of 100 nm, the surface roughness of the PET substrate can be reduced to a very small value of 0.273 nm (much less than 0.585 nm of the pure PET). Flexible white top-emitting organic light-emitting diodes (TEOLEDs) with red and blue dual phosphorescent emitting layers are constructed based on a low-reflectivity Sm/Ag semi-transparent cathode. The flexible white emission exhibits the best luminance and current injection characteristics with the 100-nm-thick MoOx buffer layer and this result indicates that a smooth substrate is beneficial to the enhancement of device electrical and electroluminescence performances. However, the white TEOLED with a 50-nm-thick MoOx buffer layer exhibits a maximum current efficiency of 4.64 cd/A and a power efficiency of 1.9 lm/W, slightly higher than those with a 100-nm MoOx buffer layer, which is mainly due to an obvious intensity enhancement but limited current increases in 50-nm MoOx-based white TEOLED. The change amplitudes of the Commission International de l'Eclairage (CIE) chromaticity coordinates are less than (0.016, 0.005) for all devices in a wide luminance range over 100 cd/m(2), indicating an excellent color stability in our white flexible TEOLEDs. Additionally, the flexible white TEOLED with an MoOx buffer layer shows excellent flexibility to withstand more than 500 bending times under a curvature radius of approximately 9 mm. Research demonstrates that it is mainly attributed to the high surface energy of the MoOx buffer layer, which is conducible to the improvement of the surface adhesion to the PET substrate and the Ag anode.

High-efficiency Flexible Organic Light-Emitting Diodes on Nanoimprinted PET Substrate

Flexible organic light-emitting diodes with enhanced light out-coupling efficiency fabricated on a double-sided nanotextured substrate.

Study of Flexible Organic Light-emitting Devices

UV-Curable Polymer-Treated Polydimethylsiloxane Substrate for Ultrahigh-Efficient Flexible Organic Light-Emitting Diodes

Flexible Substrates with Polyimide Buffer Layers for Organic Light-Emitting Diodes

Flexible Organic Light-Emitting Diodes with ITO/Ag/ITO Multi-Layers As Anodes

Flexible Top-Emitting Electroluminescent Devices on Polyethylene Terephthalate Substrates

High-performance Flexible Organic Light-Emitting Diodes Using Embedded Silver Network Transparent Electrodes.

Light Outcoupling Enhanced Flexible Organic Light-Emitting Diodes

Fabrication and property of conductive substrate for flexible organic light-emitting devices

Outcoupling-Enhanced Flexible Organic Light-Emitting Diodes on Ameliorated Plastic Substrate with Built-in Indium–Tin-Oxide-Free Transparent Electrode

Flexible Organic Light-Emitting Diodes with Improved Performance by Insertion of an UV-sensitive Layer

Extremely Efficient Transparent Flexible Organic Light-Emitting Diodes with Nanostructured Composite Electrodes

Flexible White Top-Emitting Organic Light-Emitting Diode with a MoOxroughness Improvement Layer

Highly Efficient Inkjet Printed Flexible Organic Light-Emitting Diodes with Hybrid Hole Injection Layer

High-performance Flexible Oleds on Outcoupling Enhanced Plastics

Toward Novel Flexible Display - Top-Emitting OLEDs on Al-Laminated PET Substrates

Flexible Tandem White Organic Light‐Emitting Devices with over 46% External Quantum Efficiency Via Integrating Efficient Light Outcoupling Structures

Flexible Organic Light-Emitting Diodes with Poly-3,4-ethylene- Dioxythiophene As Transparent Anode

An Efficient Flexible White Organic Light-Emitting Device with A Screen-Printed Conducting Polymer Anode

An Efficient Top-Emitting Electroluminescent Device on Metal-Laminated Plastic Substrate