Abstract:Macroporous materials polymerized from high internal phase emulsions (PolyHIPEs) possess well-defined interconnected porous structures and tunable device shapes. This provides interesting property characteristics well-suited for a variety of applications. However, such materials also demonstrate poor mechanical performances, which limit their potential use. As will be demonstrated, this results from the high surfactant content required by PolyHIPEs. Herein, a new approach is introduced for designing a highly efficient polymeric surfactant, which generates interconnected pores in PolyHIPEs through designing an incompatible surfactant and skeleton material. The surfactant also possesses a hyperbranched topology, which combines the strong amphipathy of small molecular surfactants and the nanosphere structure of Pickering emulsifiers to provide an excellent colloidal stability to HIPEs. A hyperbranched polyethylene having pendant sodium sulfonate groups (HBPE-SO3Na) was thus designed and synthesized via chain walking copolymerization of ethylene and 2-trimethylsilyloxyethyl acrylate followed by sulfonation. Stable HIPEs of styrene/divinylbenzene and water at a weight ratio of 1 to 5 were obtained with using HBPE-SO3Na. The polymerization of HIPEs produced interconnected macroporous polystyrenes (PSs) at a substantially lower surfactant content, for example, 0.5 wt % HBPE-SO3Na. The compressive Young's moduli of PolyHIPEs reached 104-111 MPa with 0.5-2 wt % HBPE-SO3Na, which is the first reported case of a PS-based PolyHIPE achieving its theoretical modulus. The PolyHIPE was used to support Au nanoparticles and embed in a column for oxidation of dimethylphenylsilane. A complete conversion of dimethylphenylsilanol was achieved with low column back pressure in a 50 h continuous reaction with no degradation of PolyHIPE integrity and mechanical property.

Synthesis of Emulsion-Templated Macroporous Materials Via Diels-Alder Polymerization

Development of Novel Materials from Polymerization of Pickering Emulsion Templates

Toward Maximizing the Mechanical Property of Interconnected Macroporous Polystyrenes Made from High Internal Phase Emulsions.

Construction Of Functional Macromolecules With Well-Defined Structures By Indium-Catalyzed Three-Component Polycoupling Of Alkynes, Aldehydes, And Amines

One-Pot Interfacial Polymerization to Prepare Polyhipes with Functional Surface

Macroporous Polymers with Aligned Microporous Walls from Pickering High Internal Phase Emulsions

Synthesis of Emulsion-templated Porous Polycaprolactone

Preparation of Macroporous Polymers from Microcapsule-Stabilized Pickering High Internal Phase Emulsions.

2021 pioneering investigator issue: mesoporous polyetherimide thin films <i>via</i> hydrolysis of polylactide-<i>b</i>-polyetherimide-<i>b</i>-polylactide

Preparation of Imide-based Microporous Organic Polymers by Alternating Free Radical Copolymerization

Hierarchical polymerized high internal phase emulsions synthesized from surfactant-stabilized emulsion templates

Synthesis of Open Porous Emulsion-Templated Monoliths Using Cetyltrimethylammonium Bromide

Interconnected Porous Polymers with Tunable Pore Throat Size Prepared Via Pickering High Internal Phase Emulsions

Mesoporous polyetherimide thin films via hydrolysis of polylactide-b-polyetherimide-b-polylactide

Macroporous Polymers Prepared Via Frozen UV Polymerization of the Emulsion-Templates Stabilized by a Low Amount of Surfactant

Hydrophilic Macroporous Monoliths with Tunable Water Uptake Capacity Fabricated by Water‐in‐oil High Internal Phase Emulsion Templating

Highly Macroporous Polyimide with Chemical Versatility Prepared from Poly(amic acid) Salt-Stabilized High Internal Phase Emulsion Template

Influence of the Macromolecular Surfactant Features and Reactivity on Morphology and Surface Properties of Emulsion-Templated Porous Polymers

Mechanism of Interconnected Pore Formation in High Internal Phase Emulsion-Templated Polymer

Engineering Bicontinuous Polymeric Monoliths Through High Internal Phase Emulsion Templating

Preparation, Characterization And Selective Solubility Of Diels-Alder Addition Polyimides