Abstract:Ni component can be effectively introduced into CeO2 by a soft template method to prepare porous NiCe composite catalysts. The reducibility of the catalyst precursors was studied by H2‐TPR. The physicochemical properties of the prepared NiCe composite catalysts were characterized by XRD, quasi in‐situ XPS, BET and TEM. And the catalytic performances of the corresponding NiCe composite catalysts was evaluated by CO2 catalytic hydrogenation. The synergistic effect of Ni and Ce species can significantly improve the reducibility of the precursors to form CO2 hydrogenation active sites in the corresponding NiCe composite catalysts. The morphology, pore structure, specific surface area, crystallinity and content of metal Ni species of the prepared NiCe composite catalysts were significantly affected by nNi/nCe ratio, which can affect the CO2 catalytic hydrogenation performances of NiCe composite catalysts. The synergistic effect of Ni and Ce species can also promote the formation of NiCe composite catalyst nanoparticles with small particle size about 5–10 nm. The developed mesoporous structure and high specific surface area can be formed in the prepared NiCe composite catalysts. The NC3 catalyst with a nNi/nCe ratio of 3.0 showed the best CO2 hydroreduction performances and use stability. When the reaction temperature was 300 °C, the CO2 conversion and CH4 selectivity can reach 85.6% and 100%, respectively. Even if the reaction temperature rises to 340 °C, the CO2 conversion and CH4 selectivity can be maintained at 83.7% and 100% in the continuous reaction of 600 min, respectively. NiCe composite catalysts with high specific surface area and developed mesoporous structure were prepared by a soft template method. The synergistic effect of Ni and Ce species can significantly improve the CO2 hydrogenation active sites to be formed.

Ceria Supported Nickel Catalysts for CO Removal from H2-rich Gas

Ceria engineering in nickel catalysts to improve CH 4 selectivity and yield for CO methanation

Ceria-supported Ni catalyst with high catalytic activity, selectivity and stability for CO 2 conversion to CH 4 by hydrogenation reaction investigated by X-ray absorption spectroscopy

Preferential Oxidation of CO and Its Subsequent Methanation in H2-rich Gas over CuO–NiO/CeO2 Catalysts

CO2 methanation on Ni-Ce0.8M0.2O2 (M=Zr, Sn or Ti) catalyst: Suppression of CO via formation of bridging carbonyls on nickel

CO2 Methanation on the Catalyst of Ni/MCM-41 Promoted with CeO2

CO Removal Via Selective Methanation over the Catalysts Ni/ZrO2 Prepared with Reduction by the Wet H-2-rich Gas

Rational design of nickel-based catalyst coupling with combined methane reforming to steadily produce syngas

Catalytic performance of Ni catalysts supported on CeO2 with different morphologies for low-temperature CO2 methanation

Synthesis Gas Production in the Combined CO2 Reforming with Partial Oxidation of Methane over Ce-promoted Ni/SiO2 Catalysts

Highly active Ni/CeO2 catalyst for CO2 methanation: Preparation and characterization

Reduced graphene oxide supported Ni-Ce catalysts for CO2 methanation: The support and ceria promotion effects

DEVELOPMENT OF SUPPORTED NICKEL-CERIUM CATALYSTS FOR RESOURCE-SAVING CONVERSION OF METHANE INTO HYDROGEN-CONTAINING GAS

Nanostructured Ni/CeO₂-ZrO₂ Catalysts for CO₂ Conversion into Synthetic Natural Gas

CO2 methanation over nickel-CeO2 catalyst supported on Al2O3: Different impregnation strategies and Ni-Ce ratios

CO2 hydrogenation to methane over Ni/ZrO2 and Ni/CeO2 catalysts: experimental and DFT studies

Role of CeO2 in Ni/CeO2–Al2O3 catalysts for carbon dioxide reforming of methane

Ce0.5Zr0.5O2 Solid Solutions Supported Co-Ni Catalyst for Ammonia Oxidative Decomposition to Hydrogen

Highly active Ni/CeO2/SiO2 catalyst for low-temperature CO2 methanation: Synergistic effect of small Ni particles and optimal amount of CeO2

Preparation of Porous NiCe Composite Catalyst and Its Performance for CO 2 Hydrogenation

Methane Reforming with Co2 to Syngas over Ceo2-Promoted Ni/Al2o3-Zro2 Catalysts Prepared Via A Direct Sol-Gel Process