Experimental study on stress corrosion crack propagation rate of FV520B in carbon dioxide and hydrogen sulfide solution

Ming Qin,Jianfeng Li,Songying Chen,Yanpeng Qu
DOI: https://doi.org/10.1016/j.rinp.2016.06.012
IF: 4.565
2016-01-01
Results in Physics
Abstract:FV520B steel is a kind of precipitation hardening Martensitic stainless steel, it has high-strength, good plasticity and good corrosion resistance. Stress corrosion cracking (SCC) is one of the main corrosion failure mode for FV520B in industrial transportation of natural gas operation. For a better understanding the effect on SCC of FV520B, the improved wedge opening loading (WOL) specimens and constant displacement loading methods were employed in experimental research in carbon dioxide and hydrogen sulfide solution. The test results showed that the crack propagation rate is 1.941 x 10(-7)-5.748 x 10(-7) mm/s, the stress intensity factor K-ISCC is not more than 36.83 MPa root m. The rate increases with the increasing of the crack opening displacement. Under the condition of different initial loading, K-ISCC generally shows a decreasing tendency with the increase in H2S concentration, and the crack propagation rate showed an increasing trend substantially. For the enrichment of sulfur ion in the crack tip induced the generation of pitting corrosion, promoting the surrounding metal formed the corrosion micro batteries, the pit defects gradually extended and connected with the adjacent pit to form a small crack, leading to further propagation till cracking happened. Fracture microscopic morphology displayed typical brittle fracture phenomena, accompanying with trans-granular cracking, river shape and sector, many second cracks on the fracture surface. (C) 2016 The Author(s). Published by Elsevier B.V.
What problem does this paper attempt to address?