Structure analysis and Raman spectroscopy of La-doped Na0.5Bi(4.5−x)LaxTi4O15 ceramics
Pooja,Neetu Ahlawat,Deepak,Kanika Rani,Deepa,Aarti,Navneet Ahlawat
DOI: https://doi.org/10.1007/s10854-024-12941-6
2024-06-25
Journal of Materials Science Materials in Electronics
Abstract:Four layer-structured Sodium Bismuth Titanate Aurivillius ferroelectric ceramics with composition Na 0.5 Bi 4.5− x La x Ti 4 O 15 ( x = 0.0, 0.25, 0.5, 0.75 and 1.0) were prepared using conventional solid state reaction method. The existence of main diffraction peak (119), confirms the four layer structure which corresponds to the highest diffraction peak (112 m + 1) observed in typical BLSF's XRD pattern. The co-existence of orthorhombic and tetragonal symmetry is validated with splitting observed in diffraction peak (200/020) and merging of these diffraction peaks at La rich compositions advocate structural transformation leading towards tetragonal symmetry. Williamson–Hall method was used to enumerate the crystallite size and micro strain, with the appropriate consideration of peak broadening parameters of individual peaks. Plate like grain evolution in microstructure of prepared samples were identified with images obtained from Field emission scanning electron microscope (FESEM). Deconvolution of the obtained Raman curves were done into their individual Gaussian components and different modes were obtained around 78, 102, 142, 221, 265, 345, 462, 552 ,736 and 854 cm −1 . The modes obtained below 200 cm −1 are low frequency modes which are assumed to be due to A-site distortion and modes obtained above 200 cm −1 are high frequency modes which are due to tilting and rotation of TiO 6 octahedron. The blue shifting of vibrational modes attribute to substitution of heavier Bi 3+ (208.9 amu) ions with comparatively lighter element La 3+ (138.9 amu). The present study revealed that presence of La ions in four layer structured lead to tetragonal symmetry and optimum polarizability can be achieved with selective concentration of La ( x = 0.75 ) in present BLSF.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied