Comonomer Inclusion in Single Crystals of Isodimorphic Random Copolymers of Butylene Succinate and ε-Caprolactone
Wenxian Hu,Maryam Safari,Yong Zhou,Ricardo A. Pérez-Camargo,Guoming Liu,Alejandro J. Müller,Dujin Wang,Ricardo A. Pérez-Camargo,Alejandro J. Müller
DOI: https://doi.org/10.1021/acs.macromol.3c00404
IF: 5.5
2023-06-21
Macromolecules
Abstract:Random copolymers exhibit diverse crystallization behavior depending on whether comonomers are excluded or included in the crystalline phase. To understand the crystallization behavior of crystallizable isodimorphic random copolymer, in this work, we selected poly[(butylene succinate)-ran-(ε-caprolactone)], BS x CL y , copolyesters and studied their single crystal structure and morphology. The single crystals of PBS homopolymer and BS-rich copolymers were prepared by the self-seeding method in o-dichlorobenzene. The prepared single crystals were characterized by atomic force microscopy (AFM) and transmission electron microscopy. The suitable seeding temperature and the dissolution temperature of the copolymers decreased with the comonomer content. The morphological features, including size, shape, layer number, and thickness, of the single crystals depend on the seeding temperature, crystallization temperature, and, most interestingly, the composition. The size of the single crystals increased with the seeding temperature, while the aspect ratio increased with the crystallization temperature. Higher CL content in the copolymers contributed to multilayered crystals and curved edges. These characteristics were explained by the difference in growth rate and the number of dislocations, both of which are expected to be influenced by the comonomers. As revealed by AFM, the thickness of the single crystals increased with CL contents, which is the opposite of what has been reported for copolymers with high degree of comonomer exclusion. Electron diffraction of the single crystals showed smaller lattice expansion as compared to melt crystallized samples, indicating a lower degree of comonomer inclusion of CL units.
polymer science