FABRICATION AND PERFORMANCE OF LEAD LANTHANUM ZIRCONATE TITANATE PIEZOELECTRIC CERAMIC FIBER

徐玲芳,陈文,周静,杨昌平

DOI: https://doi.org/10.14062/j.issn.0454-5648.2010.03.024

2010-01-01

Abstract:Lead lanthanum zirconate titanate((Pb1-xLax)(Zr1-yTiy) O3,PLZT) piezoelectric ceramic was used as raw material,and PLZT fibers with different sections was created using the plastic polymer process.The phase structure,microstructure,density,as well as mechanical and ferroelectric properties were measured with the X-ray diffraction,scanning electron microscope,density instruments,microtester instruments,and ferroelectric analyzers,respectively.As a result,the PLZT fibers are found to have trigonal perovskite phase.The diameter of the column fiber and side length of rectangular column fiber are 250μm and 300μm,respectively. The ultimate tensile strength and elastic modulus of column and rectangular column fibers are 24.88 MPa,6.90×103MPa and 23.97 MPa,5.71×10 3 MPa,respectively.All fibers have fine ferroelectric performances.The saturation field,remnant polarization(Pr) and coercive field(Ec) of column fiber are 10 kV/mm,41.40μC/cm 2 and 1.10 kV/mm,respectively.The saturation field,Pr and Ec of rectangular column fiber are 10 kV/mm,41.68μC/cm2and 1.03 kV/mm.