Controllable Hydrolysis Performance Of Mgli Alloys And Their Hydrides

Jun Jiang,Liuzhang Ouyang,Hui Wang,Jiangwen Liu,Huaiyu Shao,Min Zhu
DOI: https://doi.org/10.1002/cphc.201900058
IF: 3.52
2019-01-01
ChemPhysChem
Abstract:Theoretically, the hydrolysis of MgLi and MgH2-LiH can produce 9.6 and 17.5wt.% hydrogen (water is not included in the calculation), respectively. The ball-milling method is commonly used to refine the particle size and thus may improve hydrolysis kinetics. However, Mg and Li will be easily agglomerated, which means that direct ball-milling could not refine MgLi. In this work, we introduced 10wt.% expanded graphite into the ball-milling process to synthesize refined MgLi alloy samples. Further studies showed that MgLi-10wt.% expanded graphite can produce 966mL/g hydrogen within 3min in 0.5M MgCl2 solution. The MgLi hydrides were synthesized by reactive ball milling under 3MPa H-2 and their hydrolysis performance was investigated. Moreover, the sawed powder was milled in 3MPa H-2 for 6h and then hydrogenated in 3MPa H-2 at 380 degrees C; it can produce 1542 and 1773mL/g (15.8wt.%) hydrogen in 5 and 30min with mild kinetics, respectively, and the activation energy of the hydrolysis reaction is 24.6kJ/mol in 1M MgCl2 solution. The findings here open a new avenue to the development of refined MgLi alloys and hydrides for hydrogen generation through a controllable hydrolysis process.
What problem does this paper attempt to address?