Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Application and Research Progress of TiO_2 Nanotube Arrays with Multiple Modifications

Photo-Induced Charge Generation of TiO<sub>2</sub> Nanotube Modified with Polymer Containing C<sub>60</sub> under Irradiation of Visible Light and its Applications

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Photocatalysis with TiO2 Nanotubes: Colorful Reactivity and Designing Site-Specific Photocatalytic Centers into TiO2 Nanotubes

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

New progress in the research on the modification of TiO2 thin film

Structural evolution of anodized TiO2 nanotubes and their solar energy applications

Modified Nano-TiO2 Based Composites for Environmental Photocatalytic Applications

Photocatalysis of Nanosized TiO2 and Progress in its Application Research

The Properties, Applications and Preparations of Nanometer TiO2 Particles

A Review on the Progress of Optoelectronic Devices Based on TiO2 Thin Films and Nanomaterials

Enhanced Photoelectrochemical Property of TiO 2 Nanotube Array Photoanode Deposited with Al,Cr-Codoped SrTiO 3 Nanocubes

One-dimensional Titanium Dioxide Nanomaterials: Nanotubes

Enhanced Photoelectrochemical Properties of Ta-TiO2 Nanotube Arrays Prepared by Magnetron Sputtering

Review of the progress in preparing nano TiO2: An important environmental engineering material

Microstructured Arrays of Tio2 Nanotubes for Improved Photo-Electrocatalysis and Mechanical Stability

Application of Nanostructured TiO 2 in UV Photodetectors: A Review

Recent Advances in Black TiO2 Nanomaterials for Solar Energy Conversion

Research Developments in Semiconductor TiO2 Catalyst and Its Organic Photosensiting

Developments on Quantum Dots Sensitized TiO2 Nanotubes

Recent Advances in Anodically Fabricated Amorphous TiO2 Nanotubes Crystallization Techniques and Their Applications